Yb-Doped ZnSe nanoparticles: Synthesis, physical properties and photocatalytic activity

In this study, Yb-doped ZnSe nanoparticles were synthesized by co-reduction method at 150 °C and pH = 12 for 24 h. The obtained materials were characterized by X-ray diffraction (XRD), UVVis diffuse reflectance spectroscopy (DRS), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Powder XRD patterns indicated that the Yb_xZn_1?xSe crystals (x =0.00- 0.10) are isostructural with ZnSe. SEM and TEM images confirmed doping of Yb³⁺into the lattice of ZnSe nanoparticles. The UV-Vis diffuse reflectance characteristics of the Yb-doped ZnSe samples were quite similar to that of the undoped sample and showed a strong photoabsorption at visible light range. The electrical conductivity of Yb-doped ZnSe nanomaterials was higher than pure ZnSe at room temperature, and increased with temperature. The photocatalytic activity of synthesized nanoparticles was investigated by the degradation of Orange II solution under visible light irradiation. It was observed that the color removal efficiency of Yb-doped ZnSe catalyst was much higher than that of pure ZnSe (26.28 and 77.10% after 120 min of treatment for ZnSe and Yb_0.06Zn_0.94Se, respectively). The results demonstrated the good photocatalytic ability of synthesized nanoparticles under visible light. Also, it was revealed that the decolorization efficiency of Orange II over Yb-doped ZnSe increased with increasing Yb loading up to 6 mol% and then decreased.