Wear behavior of as-deposited and oxidized ternary (Zr, Hf)N coatings

Erdem Atar; E. Sabri Kayali; Huseyin Cimenoglu

doi:10.1007/s11661-005-0275-0

Wear behavior of as-deposited and oxidized ternary (Zr, Hf)N coatings

Erdem Atar^*
, E. Sabri Kayali
, Huseyin Cimenoglu

^*Bu çalışma için yazışmadan sorumlu yazar

Metalurji ve Malzeme Müh.Böl.

Gebze Technical University
Istanbul Technical University

Araştırma sonucu: Dergiye katkı › Makale › bilirkişi

5 Atıf (Scopus)

Özet

In the present study, the tribological performance of ternary (Zr,Hf)N coatings, whose Hf content was varied between 0 and 21 wt pct, has been systematically examined in the as-deposited and oxidized conditions. Coatings were applied on AISI D2 tool steel plates by arc physical vapor deposition (PVD). Oxidation was conducted at 400 °C for times up to 12 hours in air. Wear tests revealed pronounced improvement in the wear resistance with increasing Hf content in the as-deposited coatings. Oxidation for 12 hours yielded more than a fourfold increase in wear resistance. The beneficial effect of Hf on wear resistance decreased upon oxidation.

Orijinal dil	İngilizce
Sayfa (başlangıç-bitiş)	2793-2800
Sayfa sayısı	8
Dergi	Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science
Hacim	36
Basın numarası	10
DOI'lar	https://doi.org/10.1007/s11661-005-0275-0
Yayın durumu	Yayınlandı - Eki 2005

Finansman

The authors gratefully acknowledge the support of the NATO TU PVD Coatings Project for supplying the equipment used in this study to the Metallurgical and Materials Engineering Department, Istanbul Technical University. The authors especially thank Mr. C. Türküz for kindly carrying out the coating treatment on the specimens.

Finansörler
North Atlantic Treaty Organization
Istanbul Teknik Üniversitesi

Belgeye Erişim

10.1007/s11661-005-0275-0

Diğer Dosyalar ve Linkler

Link to publication in Scopus

Alıntı Yap

@article{9d51fa629c0c49c4b32b98707540a2ef,

title = "Wear behavior of as-deposited and oxidized ternary (Zr, Hf)N coatings",

abstract = "In the present study, the tribological performance of ternary (Zr,Hf)N coatings, whose Hf content was varied between 0 and 21 wt pct, has been systematically examined in the as-deposited and oxidized conditions. Coatings were applied on AISI D2 tool steel plates by arc physical vapor deposition (PVD). Oxidation was conducted at 400 °C for times up to 12 hours in air. Wear tests revealed pronounced improvement in the wear resistance with increasing Hf content in the as-deposited coatings. Oxidation for 12 hours yielded more than a fourfold increase in wear resistance. The beneficial effect of Hf on wear resistance decreased upon oxidation.",

author = "Erdem Atar and Kayali, \{E. Sabri\} and Huseyin Cimenoglu",

year = "2005",

month = oct,

doi = "10.1007/s11661-005-0275-0",

language = "English",

volume = "36",

pages = "2793--2800",

journal = "Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science",

issn = "1073-5623",

publisher = "Springer",

number = "10",

}

TY - JOUR

T1 - Wear behavior of as-deposited and oxidized ternary (Zr, Hf)N coatings

AU - Atar, Erdem

AU - Kayali, E. Sabri

AU - Cimenoglu, Huseyin

PY - 2005/10

Y1 - 2005/10

N2 - In the present study, the tribological performance of ternary (Zr,Hf)N coatings, whose Hf content was varied between 0 and 21 wt pct, has been systematically examined in the as-deposited and oxidized conditions. Coatings were applied on AISI D2 tool steel plates by arc physical vapor deposition (PVD). Oxidation was conducted at 400 °C for times up to 12 hours in air. Wear tests revealed pronounced improvement in the wear resistance with increasing Hf content in the as-deposited coatings. Oxidation for 12 hours yielded more than a fourfold increase in wear resistance. The beneficial effect of Hf on wear resistance decreased upon oxidation.

AB - In the present study, the tribological performance of ternary (Zr,Hf)N coatings, whose Hf content was varied between 0 and 21 wt pct, has been systematically examined in the as-deposited and oxidized conditions. Coatings were applied on AISI D2 tool steel plates by arc physical vapor deposition (PVD). Oxidation was conducted at 400 °C for times up to 12 hours in air. Wear tests revealed pronounced improvement in the wear resistance with increasing Hf content in the as-deposited coatings. Oxidation for 12 hours yielded more than a fourfold increase in wear resistance. The beneficial effect of Hf on wear resistance decreased upon oxidation.

UR - https://www.scopus.com/pages/publications/27144518036

U2 - 10.1007/s11661-005-0275-0

DO - 10.1007/s11661-005-0275-0

M3 - Article

AN - SCOPUS:27144518036

SN - 1073-5623

VL - 36

SP - 2793

EP - 2800

JO - Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science

JF - Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science

IS - 10

ER -

Wear behavior of as-deposited and oxidized ternary (Zr, Hf)N coatings

Özet

Finansman

Belgeye Erişim

Diğer Dosyalar ve Linkler

Parmak izi

Alıntı Yap