The influence of sintering temperature on mechanical and microstructural properties of bovine hydroxyapatite

G. Goller*, F. N. Oktar, S. Agathopoulos, D. U. Tulyaganov, J. M.F. Ferreira, E. S. Kayali, I. Peker

*Bu çalışma için yazışmadan sorumlu yazar

Araştırma sonucu: ???type-name???Makalebilirkişi

16 Atıf (Scopus)

Özet

The influence of sintering temperature on densification, microstructure and the mechanical properties of bovine hydroxyapatite (BHA), produced by a calcination method, was investigated. Densification and mechanical properties increased over increasing sintering temperature in the range between 1000°C and 1300°C, and there are evidences of optimum sintering temperature at 1200°C. The measured mechanical properties indicate sintered BHA-bodies as interesting biomaterials for further investigation in biomedical applications.

Orijinal dilİngilizce
Sayfa (başlangıç-bitiş)325-328
Sayfa sayısı4
DergiKey Engineering Materials
Hacim284-286
DOI'lar
Yayın durumuYayınlandı - 2005

Parmak izi

The influence of sintering temperature on mechanical and microstructural properties of bovine hydroxyapatite' araştırma başlıklarına git. Birlikte benzersiz bir parmak izi oluştururlar.

Alıntı Yap