The influence of polyelectrolyte on the synthesis of B4C/BN nanocomposite powders via sol-gel method

Suna Avcıoğlu, Zeynep Naz Ateş, Erol Kam, Cengiz Kaya, Figen Kaya*

*Bu çalışma için yazışmadan sorumlu yazar

Araştırma sonucu: ???type-name???Makalebilirkişi

1 Atıf (Scopus)

Özet

In the present study, B4C-BN nanocomposite powders were synthesized by using the sol-gel method. To investigate the effects of polyelectrolyte on phase content, particle size, and final morphology of synthesized powders different amounts of ammonium polycarboxylate were used as a gel dispersing agent and a nitrogen source. Highly crystalline, sub-micron/micron-sized boron carbide particles with varying morphologies including polyhedral-equiaxed, belt-like, needle-like, and complex-shaped hierarchical structures were produced from the polymeric gel containing glycerine, tartaric acid, and citric acid as carbon sources, and boric acid as boron source. With the addition of ammonium polycarboxylate as a polymeric gel network modifier, nanocomposite powders containing micron-sized polyhedral-equiaxed boron carbide particles and boron nitride nanoflakes were obtained. The results indicated that the particles dimensions, crystallinity, and B4C to BN phase ratio of the synthesized powders are directly related to the preliminary formation of borate-ammonium and/or amine complexes in the polymeric gel. The SEM inspections revealed that the size of boron carbide particles tends to increase from 2 μm up to 40 μm as a function of ammonium polycarboxylate content. It was also observed that the average size and thickness of boron nitride nanoflakes within the range of 80 nm to 3 μm and 10–150 nm, respectively. B4C/BN nanocomposite powders were synthesized with up to 32% BN content using a 43 wt% ammonium polycarboxylate additive.

Orijinal dilİngilizce
Sayfa (başlangıç-bitiş)15355-15363
Sayfa sayısı9
DergiCeramics International
Hacim48
Basın numarası11
DOI'lar
Yayın durumuYayınlandı - 1 Haz 2022
Harici olarak yayınlandıEvet

Bibliyografik not

Publisher Copyright:
© 2022 Elsevier Ltd and Techna Group S.r.l.

Finansman

The authors are grateful for the financial support from The Scientific and Technological Research Council of Turkey (TUBITAK) under contract number 120M651 .

FinansörlerFinansör numarası
TUBITAK
Türkiye Bilimsel ve Teknolojik Araştırma Kurumu120M651

    Parmak izi

    The influence of polyelectrolyte on the synthesis of B4C/BN nanocomposite powders via sol-gel method' araştırma başlıklarına git. Birlikte benzersiz bir parmak izi oluştururlar.

    Alıntı Yap