Template-free microspheres decorated with Cu-Fe-NLDH for catalytic removal of gentamicin in heterogeneous electro-Fenton process

Nano-layered double hydroxide (NLDH) decorated with Fe and Cu was applied as a novel heterogeneous catalyst for catalytic degradation of gentamicin by the electro-Fenton (EF) process. The EF process was equipped with graphite plate under aeration to electrochemically generate hydrogen peroxide in the solution. The characterization analyses confirmed the suitable structure of as-synthesized Cu-Fe-NLDH to be acted as catalyst for treating the target pollutant. The comparative study showed the highest removal efficiency of 91.3% when the Cu-Fe-NLDH-equipped EF process was applied in comparison with the Fenton (50%) and the electro-oxidation alone (25.6%). The acidic pHs favored the degradation of gentamicin. Increasing the current resulted in the enhanced degradation of gentamicin, while the excessive electrolyte concentration (0.1 mol/L) and catalyst dosage (1.5 g/L) led to the tangible drop in the reactor performance. At a specified reaction time, the injection of O₃ gas enhanced the efficiency of the Cu-Fe-NLDH-equipped EF process. The presence of ethanol led to more suppressing effect than benzoquinone, indicating the dominant role of [rad]OH radical in the degradation of gentamicin compared with other free radical species such as O₂[rad]^- radical. Only 10% drop in the degradation efficiency of gentamicin was observed within 10 operational runs. The mineralization efficiency of about 77% was achieved after 300 min in terms of chemical oxygen demand (COD) removal. The intermediate byproducts generated during the destructive removal of gentamicin were also identified.