Synthesis, characterization and thermoreversible behaviours of poly(dimethyl siloxane)/poly(N-isopropyl acrylamide) semi-interpenetrating networks

Simultaneous and sequential poly(N-isopropyl acrylamide) (PNIPAAm)/poly(dimethyl siloxane) (PDMS) semi-interpenetrating polymer networks (IPNs) with different linear PDMS contents were prepared by free radical polymerization method. Their phase morphologies have been characterized by FTIR, DSC and SEM. The simultaneous semi-IPNs exhibited phase transition temperatures (T_pt) shifted higher temperature from glass transition temperatures (T_g) of their respective homopolymers, suggesting a heterophase morphology and only physical entanglement between the PNIPAAm network and linear PDMS with high molecular weight (Mn ≈ 9000 g/mol). For sequential semi-IPNs, the shift of T_pts towards lower temperature suggested that the chemical interaction between the constituents of the IPNs increased with increasing PDMS content in the network. In addition, these semi-IPNs were characterized for their thermo-sensitive behaviour by equilibrium swelling studies. The results showed that incorporation of hydrophobic PDMS polymer into the thermo- and pH-sensitive PNIPAAm and P(NIPAAm-co-IA) (itaconic acid) hydrogels by semi-IPN formation decreased swelling degrees of IPNs without affecting their LCSTs whereas addition of acrylated PDMS (Tegomer V-Si 2250) as crosslinker instead of N,N^′-methylenebisacrylamide (BIS) into the structures of these hydrogels changed their LCSTs along with their swelling degrees.