Synthesis and characterization of ZrB2 produced with molten salt electrolysis method

Selda Ozkan*, Mustafa Urgen, Servet Timur

*Bu çalışma için yazışmadan sorumlu yazar

Araştırma sonucu: ???type-name???Konferans katkısıbilirkişi

Özet

In this study, a combination of cathodic arc physical vapor deposition (PVD) and molten salt electrolysis methods were used to obtain ZrB2 layers on AISI 304 grade stainless steel surface. Prior to boriding, steel surface was coated with metallic zirconium via cathodic arc PVD method and then the zirconium coated steel was borided by molten salt electrolysis. Well adherent, dense, ZrB2 layers are formed on the substrates. The thickness of the ZrB2 layer showed dependence on the thickness of the metallic Zr coating layer and the time of boriding. During the boriding process the alloying elements of the substrate also took part in the coating structure depending on their diffusion characteristics.

Orijinal dilİngilizce
Ana bilgisayar yayını başlığıEPD Congress 2010 - Held During TMS 2010 Annual Meeting and Exhibition
Sayfalar395-401
Sayfa sayısı7
Yayın durumuYayınlandı - 2010
EtkinlikEPD Congress 2010 - TMS 2010 Annual Meeting and Exhibition - Seattle, WA, United States
Süre: 14 Şub 201018 Şub 2010

Yayın serisi

AdıTMS Annual Meeting

???event.eventtypes.event.conference???

???event.eventtypes.event.conference???EPD Congress 2010 - TMS 2010 Annual Meeting and Exhibition
Ülke/BölgeUnited States
ŞehirSeattle, WA
Periyot14/02/1018/02/10

Parmak izi

Synthesis and characterization of ZrB2 produced with molten salt electrolysis method' araştırma başlıklarına git. Birlikte benzersiz bir parmak izi oluştururlar.

Alıntı Yap