Özet
A new generation multihollow opaque polymer pigment was synthesized by suspension polymerization of "water-in-oil-in-water" emulsion method, where methyl methacrylate and ethylene glycol dimethacrylate monomer mixture was used as oil phase. The effects of surfactant and cosurfactant composition in terms of "hydrophilic/lipophilic balance" on the stability of the "water-in-oil" emulsion and the size of water droplets were studied. Low droplet sizes and the optimum stability were obtained with "Span 80&Tween 80" surfactant mixture at an HLB value of 8. The desired size distribution was obtained at "monomer/surfactant/water" ratio of 75.5/9.4/15.1 at an ultrasonic mixing power of 80 W lasting for 30 s. The surface morphology and hollow structure of polymer pigments were analyzed by scanning and transmission electron microscopy techniques. L∗a∗b color and gloss properties of polymer pigments were examined. The opacity values were assessed by contrast ratio measurements, and the pigments provided up to 97.3% opacity with 50% v/v solid content in resin. In addition, the pigments exhibited low gloss values and yielded matte films.
Orijinal dil | İngilizce |
---|---|
Makale numarası | 43696 |
Dergi | Journal of Applied Polymer Science |
Hacim | 133 |
Basın numarası | 29 |
DOI'lar | |
Yayın durumu | Yayınlandı - 5 Ağu 2016 |
Harici olarak yayınlandı | Evet |
Bibliyografik not
Publisher Copyright:© 2016 Wiley Periodicals, Inc.