Switching performance of W-Ag electrical contacts fabricated by mechanical alloying

Ziya Aslanoǧlu, Yilmaz Karakas, M. Lütfi Ovecoǧlu

Araştırma sonucu: ???type-name???Makalebilirkişi

17 Atıf (Scopus)

Özet

Blended elemental W - 35 w/o Ag powders were mechanically alloyed in a heavy duty attritor mill for times up to 15h followed by compaction, sintering, furnace cooling and re-sintering under industrial conditions. Changes in the morphology and microstructure of the as-milled powders and the compacts were characterized by scanning electron microscopy which revealed regions of nominal composition and loose W particles in the as-milled state. X-ray diffraction scans of the milled powders and compacts showed the presence of W and Ag peaks. Higher densities and hardness values were achieved for compacts mechanically alloyed at longer times. The arc erosion characteristics of the W-35w/oAg compacts confirmed that the erosion rate of the contact material decreased with increasing milling time. On the basis of a linear regression estimate, all the compacts were found to be suitable for electrical contact applications. In particular, compacts mechanically alloyed for 10h were estimated to endure more than 3 × 106 operations.

Orijinal dilİngilizce
Sayfa (başlangıç-bitiş)35-43
Sayfa sayısı9
DergiInternational Journal of Powder Metallurgy (Princeton, New Jersey)
Hacim36
Basın numarası8
Yayın durumuYayınlandı - Kas 2000
Harici olarak yayınlandıEvet

Parmak izi

Switching performance of W-Ag electrical contacts fabricated by mechanical alloying' araştırma başlıklarına git. Birlikte benzersiz bir parmak izi oluştururlar.

Alıntı Yap