Surface characteristics of low-temperature gas nitrided 316 Ti austenitic stainless steels

Ozgur Celik*, Eyup Sabri Kayali, Huseyin Cimenoglu

*Bu çalışma için yazışmadan sorumlu yazar

Araştırma sonucu: Kitap/Rapor/Konferans Bildirisinde BölümKonferans katkısıbilirkişi

Özet

Uniform, compact and precipitate free hybrid solution layer (nitrogen and carbon rich) was succesfully formed on the surface of a 316Ti austenitic stainless steel by low temperature nitriding process (below 450 °C) in a fluidized bed furnace. After the nitriding, 316 Ti austenitic steel exhibited extremely high surface hardness (1690 HV0.05) when compared to the hardness of as-received state (295 HV0.05). Formation of solid solution layer, which did not lead any embrittlement effect during tensile and bending tests, enhanced the pitting corrosion resistance, remarkably.

Orijinal dilİngilizce
Ana bilgisayar yayını başlığıTMS 2009 - 138th Annual Meeting and Exhibition - Supplemental Proceedings
Sayfalar305-311
Sayfa sayısı7
Yayın durumuYayınlandı - 2009
EtkinlikTMS 2009 - 138th Annual Meeting and Exhibition - San Francisco, CA, United States
Süre: 15 Şub 200919 Şub 2009

Yayın serisi

AdıTMS Annual Meeting
Hacim3

???event.eventtypes.event.conference???

???event.eventtypes.event.conference???TMS 2009 - 138th Annual Meeting and Exhibition
Ülke/BölgeUnited States
ŞehirSan Francisco, CA
Periyot15/02/0919/02/09

Parmak izi

Surface characteristics of low-temperature gas nitrided 316 Ti austenitic stainless steels' araştırma başlıklarına git. Birlikte benzersiz bir parmak izi oluştururlar.

Alıntı Yap