Super enhancement of rheological properties of amorphous PLA through generation of a fiberlike oriented crystal network

Mohammadreza Nofar*, Mojtaba Mohammadi, Pierre J. Carreau

*Bu çalışma için yazışmadan sorumlu yazar

Araştırma sonucu: ???type-name???Makalebilirkişi

8 Atıf (Scopus)

Özet

Blends containing 85 wt. % of an amorphous polylactide with 15 wt. % of three different semicrystalline PLA (cPLA) grades with different crystallizabilty were separately blended via a twin-screw extruder below the melting temperature of the cPLAs. The extrudates were either directly pelletized or pelletized after being drawn at a draw ratio of 10. The small amplitude oscillatory shear behavior of the samples revealed that while the rheological properties of the undrawn samples were enhanced, those of the drawn samples were much more dramatically increased. In undrawn samples, the enhancements were due to the presence of unmelted crystal clusters, which could form a solid network structure in the blend. The much more pronounced increases in drawn samples, however, were due to the transformation of the crystal clusters into the fiberlike oriented crystal network, which formed a stronger solid network. This reinforcing behavior in both undrawn and drawn samples was even more pronounced when cPLA with a higher degree of crystallinity and a higher melting temperature was used. In drawn samples, the stress growth experiments confirmed the formation of such oriented crystal structure during which the primary overshoot caused by the crystal network structure could be formed again after molecular relaxation. This was while, in undrawn samples, stress overshoots were barely visible.

Orijinal dilİngilizce
Sayfa (başlangıç-bitiş)493-505
Sayfa sayısı13
DergiJournal of Rheology
Hacim65
Basın numarası4
DOI'lar
Yayın durumuYayınlandı - 1 Tem 2021

Bibliyografik not

Publisher Copyright:
© 2021 The Society of Rheology.

Parmak izi

Super enhancement of rheological properties of amorphous PLA through generation of a fiberlike oriented crystal network' araştırma başlıklarına git. Birlikte benzersiz bir parmak izi oluştururlar.

Alıntı Yap