Özet

In the present work, multi-cation doped (Sr2+-Mn4+) SiAlON ceramics were investigated. The mixture was sintered at in a gas pressure sintering furnace (GPS). XRD results showed that sintered samples were composed of β and α-SiAlON phases and this result is also confirmed by back scattered SEM images. EDX analysis of the individual α-SiAlON grains showed that Mn can incorporate into the α-SiAlON structure when it is codoped with Sr.

Orijinal dil	İngilizce
Sayfa sayısı	4
DOI'lar	https://doi.org/10.4028/www.scientific.net/ast.45.73
Yayın durumu	Yayınlandı - Eki 2006

Belgeye Erişim

10.4028/www.scientific.net/ast.45.73

Diğer Dosyalar ve Linkler

Alıntı Yap

@conference{282071aacb6e4625970360d9ead577ff,

title = "Sr2+ - Mn4+ Doped SiAION Ceramics",

abstract = "In the present work, multi-cation doped (Sr2+-Mn4+) SiAlON ceramics were investigated. The mixture was sintered at in a gas pressure sintering furnace (GPS). XRD results showed that sintered samples were composed of β and α-SiAlON phases and this result is also confirmed by back scattered SEM images. EDX analysis of the individual α-SiAlON grains showed that Mn can incorporate into the α-SiAlON structure when it is codoped with Sr.",

author = "B. Akin and S.R. Kushan and Hasan Mandal",

year = "2006",

month = oct,

doi = "10.4028/www.scientific.net/ast.45.73",

language = "English",

}

TY - CONF

T1 - Sr2+ - Mn4+ Doped SiAION Ceramics

AU - Akin, B.

AU - Kushan, S.R.

AU - Mandal, Hasan

PY - 2006/10

Y1 - 2006/10

N2 - In the present work, multi-cation doped (Sr2+-Mn4+) SiAlON ceramics were investigated. The mixture was sintered at in a gas pressure sintering furnace (GPS). XRD results showed that sintered samples were composed of β and α-SiAlON phases and this result is also confirmed by back scattered SEM images. EDX analysis of the individual α-SiAlON grains showed that Mn can incorporate into the α-SiAlON structure when it is codoped with Sr.

AB - In the present work, multi-cation doped (Sr2+-Mn4+) SiAlON ceramics were investigated. The mixture was sintered at in a gas pressure sintering furnace (GPS). XRD results showed that sintered samples were composed of β and α-SiAlON phases and this result is also confirmed by back scattered SEM images. EDX analysis of the individual α-SiAlON grains showed that Mn can incorporate into the α-SiAlON structure when it is codoped with Sr.

UR - https://www.mendeley.com/catalogue/9e70e92c-cf19-382c-b42d-84910536187b/

U2 - 10.4028/www.scientific.net/ast.45.73

DO - 10.4028/www.scientific.net/ast.45.73

M3 - Paper