In the present work, multi-cation-doped (Sr²⁺-Mg²⁺) SiAlON ceramics were investigated. MgO and SrO were used in 100:0 and 50:50 molar ratios. The mixture was sintered at 1800°and 1830°C for 1 h in a gas pressure-sintering furnace. The results showed that sintered samples were composed of mainly α- and β-SiAlON phases and small amounts of some Sr-containing phases and SiAlON polytypes. According to Rietveld analysis of X-ray diffraction patterns, Mg is incorporated into the α-SiAlON structure. However, the incorporation of Sr is limited.

Orijinal dil	İngilizce
Sayfa (başlangıç-bitiş)	714-716
Sayfa sayısı	3
Dergi	Journal of the American Ceramic Society
Hacim	89
Basın numarası	2
DOI'lar	https://doi.org/10.1111/j.1551-2916.2005.00749.x
Yayın durumu	Yayınlandı - Şub 2006
Harici olarak yayınlandı	Evet

Belgeye Erişim

10.1111/j.1551-2916.2005.00749.x

Diğer Dosyalar ve Linkler

Link to publication in Scopus

Alıntı Yap

@article{f8370d2b99134117aae03d20ad61bc23,

title = "Sr2+-Mg2+-doped SiAlON ceramics",

abstract = "In the present work, multi-cation-doped (Sr2+-Mg2+) SiAlON ceramics were investigated. MgO and SrO were used in 100:0 and 50:50 molar ratios. The mixture was sintered at 1800°and 1830°C for 1 h in a gas pressure-sintering furnace. The results showed that sintered samples were composed of mainly α- and β-SiAlON phases and small amounts of some Sr-containing phases and SiAlON polytypes. According to Rietveld analysis of X-ray diffraction patterns, Mg is incorporated into the α-SiAlON structure. However, the incorporation of Sr is limited.",

author = "Semra Kurama and Gunes Cigdemir and Hasan Mandal and Mathias Herrmann",

year = "2006",

month = feb,

doi = "10.1111/j.1551-2916.2005.00749.x",

language = "English",

volume = "89",

pages = "714--716",

journal = "Journal of the American Ceramic Society",

issn = "0002-7820",

publisher = "Wiley-Blackwell",

number = "2",

}

TY - JOUR

T1 - Sr2+-Mg2+-doped SiAlON ceramics

AU - Kurama, Semra

AU - Cigdemir, Gunes

AU - Mandal, Hasan

AU - Herrmann, Mathias

PY - 2006/2

Y1 - 2006/2

N2 - In the present work, multi-cation-doped (Sr2+-Mg2+) SiAlON ceramics were investigated. MgO and SrO were used in 100:0 and 50:50 molar ratios. The mixture was sintered at 1800°and 1830°C for 1 h in a gas pressure-sintering furnace. The results showed that sintered samples were composed of mainly α- and β-SiAlON phases and small amounts of some Sr-containing phases and SiAlON polytypes. According to Rietveld analysis of X-ray diffraction patterns, Mg is incorporated into the α-SiAlON structure. However, the incorporation of Sr is limited.

AB - In the present work, multi-cation-doped (Sr2+-Mg2+) SiAlON ceramics were investigated. MgO and SrO were used in 100:0 and 50:50 molar ratios. The mixture was sintered at 1800°and 1830°C for 1 h in a gas pressure-sintering furnace. The results showed that sintered samples were composed of mainly α- and β-SiAlON phases and small amounts of some Sr-containing phases and SiAlON polytypes. According to Rietveld analysis of X-ray diffraction patterns, Mg is incorporated into the α-SiAlON structure. However, the incorporation of Sr is limited.

UR - http://www.scopus.com/inward/record.url?scp=33645148326&partnerID=8YFLogxK

U2 - 10.1111/j.1551-2916.2005.00749.x

DO - 10.1111/j.1551-2916.2005.00749.x

M3 - Article

AN - SCOPUS:33645148326

SN - 0002-7820

VL - 89

SP - 714

EP - 716

JO - Journal of the American Ceramic Society

JF - Journal of the American Ceramic Society

IS - 2