Spectral Investigation of Yb3+/Ho3+/Tm3+:Y2Si2O7 Upconverting Nanophosphors for the Usage of Temperature Sensing

Murat Erdem*, Kadir Esmer, Gonul Eryurek

*Bu çalışma için yazışmadan sorumlu yazar

Araştırma sonucu: ???type-name???Makalebilirkişi

1 Atıf (Scopus)

Özet

Rare earth (Yb3+, Ho3+, Tm3+) yttrium disilicate phosphors were produced by sol-gel technique and heated at 1050 °C temperature. The sizes of the phosphors vary between 20-30 nm according to the images obtained from the Transmission Electron Microscope. The up-conversion (UC) emissions of the nanopowders were measured in the range of 500–900 nm wavelength under 950 nm laser excitation. A linear increase with power was observed in the emission intensity ratio depending on the laser excitation power. Using the FIR technique, the phosphor’s temperature was determined by the heating effect caused by the laser pump power. Due to the change in intensity ratio versus temperature, the temperature sensitivity at 428 K was calculated as 0.781x10-2K-1 and it was suggested that it can be used as a promising temperature sensor probe in photonic devices.

Orijinal dilİngilizce
Sayfa (başlangıç-bitiş)55-62
Sayfa sayısı8
DergiJournal of the Turkish Chemical Society, Section A: Chemistry
Hacim10
Basın numarası1
DOI'lar
Yayın durumuYayınlandı - 28 Şub 2023

Bibliyografik not

Publisher Copyright:
© 2023, Turkish Chemical Society. All rights reserved.

Finansman

The study was carried out with the support of the Marmara University Scientific Research Projects Unit, project number FEN-B-150513-0170. We thank Prof. Dr. Baldassare Di Bartolo for the photoluminescent measurements performed in the Spectroscopy Laboratory at Boston College.

FinansörlerFinansör numarası
Marmara ÜniversitesiFEN-B-150513-0170

    Parmak izi

    Spectral Investigation of Yb3+/Ho3+/Tm3+:Y2Si2O7 Upconverting Nanophosphors for the Usage of Temperature Sensing' araştırma başlıklarına git. Birlikte benzersiz bir parmak izi oluştururlar.

    Alıntı Yap