Sod-ZMOF/Matrimid® mixed matrix membranes for CO2 separation

Ayşe Kiliç, Çiğdem Atalay-Oral, Ahmet Sirkecioğlu, S. Birgül Tantekin-Ersolmaz, M. Göktuğ Ahunbay*

*Bu çalışma için yazışmadan sorumlu yazar

Araştırma sonucu: Dergiye katkıMakalebilirkişi

39 Atıf (Scopus)

Özet

In this study, sod-ZMOF (zeolite-like metal organic framework with sodalite topology) crystals were synthesized in order to prepare polymer/sod-ZMOF mixed matrix membranes (MMMs) for CO2/CH4 separation. The sod-ZMOF crystals were then incorporated into Matrimid® polyimide matrix to form dense MMMs by a solvent-casting method. After the analyses of structural and thermal characteristics of the prepared membranes, their CO2/CH4 separation performances were determined by measuring single and mixed gas permeabilities with a constant volume-variable pressure method at steady-state. SEM images of the MMMs showed that ZMOF particles were dispersed homogeneously in the polymer matrix and there were no significant voids or defects at the filler/polymer interface. While single gas permeability measurements of the membranes showed that CH4 and CO2 permeability increased without any significant change in the ideal selectivity, binary gas permeability measurements indicated that both CO2 permeability and selectivity were enhanced, with the increasing amount of incorporated MOF indicating strong adsorption selectivity of sod-ZMOF for CO2.

Orijinal dilİngilizce
Sayfa (başlangıç-bitiş)81-89
Sayfa sayısı9
DergiJournal of Membrane Science
Hacim489
DOI'lar
Yayın durumuYayınlandı - 1 Eyl 2015

Bibliyografik not

Publisher Copyright:
© 2015 Elsevier B.V.

Finansman

This work was supported in part by the Scientific and Technological Research Council of Turkey (TUBITAK) through Grant no. 113M776 .

FinansörlerFinansör numarası
TUBITAK113M776
Türkiye Bilimsel ve Teknolojik Araştirma Kurumu

    Parmak izi

    Sod-ZMOF/Matrimid® mixed matrix membranes for CO2 separation' araştırma başlıklarına git. Birlikte benzersiz bir parmak izi oluştururlar.

    Alıntı Yap