Sliding wear behaviour of ZrN and (Zr, 12 wt% Hf)N coatings

Erdem Atar; E. Sabri Kayali; Huseyin Cimenoglu

doi:10.1016/j.triboint.2005.01.038

Sliding wear behaviour of ZrN and (Zr, 12 wt% Hf)N coatings

Erdem Atar
, E. Sabri Kayali
, Huseyin Cimenoglu^*

^*Bu çalışma için yazışmadan sorumlu yazar

Metalurji ve Malzeme Müh.Böl.

Araştırma sonucu: Dergiye katkı › Makale › bilirkişi

41 Atıf (Scopus)

Özet

In the present study, the sliding wear resistances of ZrN and (Zr, 12 wt% Hf)N coatings deposited on a hardened AISI D2 tool steel by arc-physical vapor deposition (PVD) technique were examined by a ball-on-disc wear tester. Alloying of ZrN coating with 12 wt% Hf did not change the hardness significantly, but achieved an improvement on adhesion strength and dry sliding wear resistance against steel (AISI 52100-55HRC) and Al₂O₃ balls.

Orijinal dil	İngilizce
Sayfa (başlangıç-bitiş)	297-302
Sayfa sayısı	6
Dergi	Tribology International
Hacim	39
Basın numarası	4
DOI'lar	https://doi.org/10.1016/j.triboint.2005.01.038
Yayın durumu	Yayınlandı - Nis 2006

Finansman

The authors gratefully acknowledge the support of NATO TU PVD Coatings Project for the equipment supplied to the Metallurgical and Material Engineering Department of Istanbul Technical University, which was utilized in this study. The authors would like to thank Mr C. Türküz for the coating of the test samples.

Finansörler
North Atlantic Treaty Organization
Istanbul Teknik Üniversitesi

Belgeye Erişim

10.1016/j.triboint.2005.01.038

Diğer Dosyalar ve Linkler

Link to publication in Scopus

Alıntı Yap

@article{09635870420a401ab4c59a4382d6374d,

title = "Sliding wear behaviour of ZrN and (Zr, 12 wt\% Hf)N coatings",

abstract = "In the present study, the sliding wear resistances of ZrN and (Zr, 12 wt\% Hf)N coatings deposited on a hardened AISI D2 tool steel by arc-physical vapor deposition (PVD) technique were examined by a ball-on-disc wear tester. Alloying of ZrN coating with 12 wt\% Hf did not change the hardness significantly, but achieved an improvement on adhesion strength and dry sliding wear resistance against steel (AISI 52100-55HRC) and Al2O3 balls.",

keywords = "Coating, Hf, PVD, Wear, ZrN",

author = "Erdem Atar and Kayali, \{E. Sabri\} and Huseyin Cimenoglu",

year = "2006",

month = apr,

doi = "10.1016/j.triboint.2005.01.038",

language = "English",

volume = "39",

pages = "297--302",

journal = "Tribology International",

issn = "0301-679X",

publisher = "Elsevier Inc.",

number = "4",

}

TY - JOUR

T1 - Sliding wear behaviour of ZrN and (Zr, 12 wt% Hf)N coatings

AU - Atar, Erdem

AU - Kayali, E. Sabri

AU - Cimenoglu, Huseyin

PY - 2006/4

Y1 - 2006/4

N2 - In the present study, the sliding wear resistances of ZrN and (Zr, 12 wt% Hf)N coatings deposited on a hardened AISI D2 tool steel by arc-physical vapor deposition (PVD) technique were examined by a ball-on-disc wear tester. Alloying of ZrN coating with 12 wt% Hf did not change the hardness significantly, but achieved an improvement on adhesion strength and dry sliding wear resistance against steel (AISI 52100-55HRC) and Al2O3 balls.

AB - In the present study, the sliding wear resistances of ZrN and (Zr, 12 wt% Hf)N coatings deposited on a hardened AISI D2 tool steel by arc-physical vapor deposition (PVD) technique were examined by a ball-on-disc wear tester. Alloying of ZrN coating with 12 wt% Hf did not change the hardness significantly, but achieved an improvement on adhesion strength and dry sliding wear resistance against steel (AISI 52100-55HRC) and Al2O3 balls.

KW - Coating

KW - Hf

KW - PVD

KW - Wear

KW - ZrN

UR - https://www.scopus.com/pages/publications/28944444409

U2 - 10.1016/j.triboint.2005.01.038

DO - 10.1016/j.triboint.2005.01.038

M3 - Article

AN - SCOPUS:28944444409

SN - 0301-679X

VL - 39

SP - 297

EP - 302

JO - Tribology International

JF - Tribology International

IS - 4

ER -

Sliding wear behaviour of ZrN and (Zr, 12 wt% Hf)N coatings

Özet

Finansman

Belgeye Erişim

Diğer Dosyalar ve Linkler

Parmak izi

Alıntı Yap