Si based anodes via magnetron sputtering for LIB

B. Deniz Polat, O. Levent Eryilmaz, Özgül Keleş

Araştırma sonucu: ???type-name???Makalebilirkişi

10 Atıf (Scopus)

Özet

The reversible cyclability of Si based anodes is greatly improved by tuning the atomic ratio of Cu/Si and the thickness of films fabricated via magnetron sputtering. High electrochemical performance is achieved when the thin film made of 10% at.Cu-90% at.Si is used. 1100 mAhg-1 specific capacity is delivered after the 100th cycles with 99.7% Coulombic efficiency. This remarkable performance is the result of the amorphous structure and enhanced physical and mechanical properties of the thin film.

Orijinal dilİngilizce
Sayfa (başlangıç-bitiş)A45-A49
DergiECS Electrochemistry Letters
Hacim3
Basın numarası6
DOI'lar
Yayın durumuYayınlandı - 2014

Parmak izi