Roasting of celestite in laboratory scale rotary furnace

Selim Ertürk; Raşit Sezer; İbrahim Göksel Hizli; Ayşegül Bilen; Cüneyt Arslan

doi:10.1007/978-3-319-51340-9_46

Roasting of celestite in laboratory scale rotary furnace

Selim Ertürk^*
, Raşit Sezer
, İbrahim Göksel Hizli
, Ayşegül Bilen
, Cüneyt Arslan

^*Bu çalışma için yazışmadan sorumlu yazar

Metalurji ve Malzeme Müh.Böl.

Istanbul Technical University
Karadeniz Technical University
Istanbul University

Araştırma çıktısı: Kitap/Rapor/Konferans Bildirisinde Bölüm › Konferans katkısı › Hakem

2 Atıf (Scopus)

Özet

Turkish celestite ore was roasted in a lab scale rotary kiln furnace with metallurgical coke. Coke and celestite were mixed; the product contained 32% coke which is more than the stoichiometric requirement. 100 g of the mixed product was fed to a rotary furnace at 35 g/min. Temperature (1000 and 1100 °C), rotation speed (2.5, 5 and 10 rpm) and the slope of the furnace (2, 3 and 5°) were among the investigated parameters. Phase and chemical analyses were carried out by XRD and XRF techniques, respectively. The maximum solubility of the roasted product in water was 48% under the roasting conditions of 1100 °C, 2.5 rpm and 2° slope.

Orijinal dil	İngilizce
Ana bilgisayar yayını başlığı	8th International Symposium on High-Temperature Metallurgical Processing, 2017
Editörler	Jiann-Yang Hwang, Mark William Kennedy, Varadarajan Seshadri, Baojun Zhao, Dean Gregurek, Tao Jiang, P. Chris Pistorius, Ender Keskinkilic, Onuralp Yucel
Yayınlayan	Springer International Publishing
Sayfalar	469-476
Sayfa sayısı	8
ISBN (Basılı)	9783319513393
DOI'lar	https://doi.org/10.1007/978-3-319-51340-9_46
Yayın durumu	Yayınlandı - 2017
Etkinlik	8th International Symposium on High-Temperature Metallurgical Processing, in conjunction with the TMS Annual Meeting and Exhibition, 2017 - San Diego, United States Süre: 26 Şub 2017 → 2 Mar 2017

Yayın serisi

Adı	Minerals, Metals and Materials Series
Hacim	Part F5
ISSN (Basılı)	2367-1181
ISSN (Elektronik)	2367-1696

???event.eventtypes.event.conference???

???event.eventtypes.event.conference???	8th International Symposium on High-Temperature Metallurgical Processing, in conjunction with the TMS Annual Meeting and Exhibition, 2017
Ülke/Bölge	United States
Şehir	San Diego
Periyot	26/02/17 → 2/03/17

Bibliyografik not

Publisher Copyright:
© The Minerals, Metals & Materials Society 2017.

Finansman

The authors greatly acknowledge the financial support provided by Scientific and Research Council of Turkey (TUBITAK) under the contract no 115M631 and would like to thank to Barit Maden Türk Ltd. for technical and materials support. Acknowledgements The authors greatly acknowledge the financial support provided by Scientific and Research Council of Turkey (TUBITAK) under the contract no 115M631 and would like to thank to Barit Maden Türk Ltd. for technical and materials support.

Finansörler	Finansör numarası
Scientific and Research Council of Turkey
TUBITAK
Türkiye Bilimsel ve Teknolojik Araştirma Kurumu	115M631

Belgeye Erişim

10.1007/978-3-319-51340-9_46

Diğer Dosyalar ve Linkler

Link to publication in Scopus

Alıntı Yap

Ertürk, S., Sezer, R., Hizli, İ. G., Bilen, A., & Arslan, C. (2017). Roasting of celestite in laboratory scale rotary furnace. In J.-Y. Hwang, M. W. Kennedy, V. Seshadri, B. Zhao, D. Gregurek, T. Jiang, P. C. Pistorius, E. Keskinkilic, & O. Yucel (Eds.), 8th International Symposium on High-Temperature Metallurgical Processing, 2017 (pp. 469-476). (Minerals, Metals and Materials Series; Hac. Part F5). Springer International Publishing. https://doi.org/10.1007/978-3-319-51340-9_46

Ertürk, Selim ; Sezer, Raşit ; Hizli, İbrahim Göksel et al. / Roasting of celestite in laboratory scale rotary furnace. 8th International Symposium on High-Temperature Metallurgical Processing, 2017. editör / Jiann-Yang Hwang ; Mark William Kennedy ; Varadarajan Seshadri ; Baojun Zhao ; Dean Gregurek ; Tao Jiang ; P. Chris Pistorius ; Ender Keskinkilic ; Onuralp Yucel. Springer International Publishing, 2017. pp. 469-476 (Minerals, Metals and Materials Series).

@inproceedings{e28963ff9cbf452ebce7760a6f8e01d6,

title = "Roasting of celestite in laboratory scale rotary furnace",

abstract = "Turkish celestite ore was roasted in a lab scale rotary kiln furnace with metallurgical coke. Coke and celestite were mixed; the product contained 32\% coke which is more than the stoichiometric requirement. 100 g of the mixed product was fed to a rotary furnace at 35 g/min. Temperature (1000 and 1100 °C), rotation speed (2.5, 5 and 10 rpm) and the slope of the furnace (2, 3 and 5°) were among the investigated parameters. Phase and chemical analyses were carried out by XRD and XRF techniques, respectively. The maximum solubility of the roasted product in water was 48\% under the roasting conditions of 1100 °C, 2.5 rpm and 2° slope.",

keywords = "Roasting, Turkish celestite",

author = "Selim Ert{\"u}rk and Ra{\c s}it Sezer and Hizli, \{İbrahim G{\"o}ksel\} and Ay{\c s}eg{\"u}l Bilen and C{\"u}neyt Arslan",

note = "Publisher Copyright: {\textcopyright} The Minerals, Metals \& Materials Society 2017.; 8th International Symposium on High-Temperature Metallurgical Processing, in conjunction with the TMS Annual Meeting and Exhibition, 2017 ; Conference date: 26-02-2017 Through 02-03-2017",

year = "2017",

doi = "10.1007/978-3-319-51340-9\_46",

language = "English",

isbn = "9783319513393",

series = "Minerals, Metals and Materials Series",

publisher = "Springer International Publishing",

pages = "469--476",

editor = "Jiann-Yang Hwang and Kennedy, \{Mark William\} and Varadarajan Seshadri and Baojun Zhao and Dean Gregurek and Tao Jiang and Pistorius, \{P. Chris\} and Ender Keskinkilic and Onuralp Yucel",

booktitle = "8th International Symposium on High-Temperature Metallurgical Processing, 2017",

address = "Switzerland",

}

Ertürk, S, Sezer, R, Hizli, İG, Bilen, A & Arslan, C 2017, Roasting of celestite in laboratory scale rotary furnace. in J-Y Hwang, MW Kennedy, V Seshadri, B Zhao, D Gregurek, T Jiang, PC Pistorius, E Keskinkilic & O Yucel (eds), 8th International Symposium on High-Temperature Metallurgical Processing, 2017. Minerals, Metals and Materials Series, hac. Part F5, Springer International Publishing, pp. 469-476, 8th International Symposium on High-Temperature Metallurgical Processing, in conjunction with the TMS Annual Meeting and Exhibition, 2017, San Diego, United States, 26/02/17. https://doi.org/10.1007/978-3-319-51340-9_46

Roasting of celestite in laboratory scale rotary furnace. / Ertürk, Selim; Sezer, Raşit; Hizli, İbrahim Göksel et al.
8th International Symposium on High-Temperature Metallurgical Processing, 2017. ed. / Jiann-Yang Hwang; Mark William Kennedy; Varadarajan Seshadri; Baojun Zhao; Dean Gregurek; Tao Jiang; P. Chris Pistorius; Ender Keskinkilic; Onuralp Yucel. Springer International Publishing, 2017. p. 469-476 (Minerals, Metals and Materials Series; Hac. Part F5).

Araştırma çıktısı: Kitap/Rapor/Konferans Bildirisinde Bölüm › Konferans katkısı › Hakem

TY - GEN

T1 - Roasting of celestite in laboratory scale rotary furnace

AU - Ertürk, Selim

AU - Sezer, Raşit

AU - Hizli, İbrahim Göksel

AU - Bilen, Ayşegül

AU - Arslan, Cüneyt

N1 - Publisher Copyright: © The Minerals, Metals & Materials Society 2017.

PY - 2017

Y1 - 2017

N2 - Turkish celestite ore was roasted in a lab scale rotary kiln furnace with metallurgical coke. Coke and celestite were mixed; the product contained 32% coke which is more than the stoichiometric requirement. 100 g of the mixed product was fed to a rotary furnace at 35 g/min. Temperature (1000 and 1100 °C), rotation speed (2.5, 5 and 10 rpm) and the slope of the furnace (2, 3 and 5°) were among the investigated parameters. Phase and chemical analyses were carried out by XRD and XRF techniques, respectively. The maximum solubility of the roasted product in water was 48% under the roasting conditions of 1100 °C, 2.5 rpm and 2° slope.

AB - Turkish celestite ore was roasted in a lab scale rotary kiln furnace with metallurgical coke. Coke and celestite were mixed; the product contained 32% coke which is more than the stoichiometric requirement. 100 g of the mixed product was fed to a rotary furnace at 35 g/min. Temperature (1000 and 1100 °C), rotation speed (2.5, 5 and 10 rpm) and the slope of the furnace (2, 3 and 5°) were among the investigated parameters. Phase and chemical analyses were carried out by XRD and XRF techniques, respectively. The maximum solubility of the roasted product in water was 48% under the roasting conditions of 1100 °C, 2.5 rpm and 2° slope.

KW - Roasting

KW - Turkish celestite

UR - https://www.scopus.com/pages/publications/85042468758

U2 - 10.1007/978-3-319-51340-9_46

DO - 10.1007/978-3-319-51340-9_46

M3 - Conference contribution

AN - SCOPUS:85042468758

SN - 9783319513393

T3 - Minerals, Metals and Materials Series

SP - 469

EP - 476

BT - 8th International Symposium on High-Temperature Metallurgical Processing, 2017

A2 - Hwang, Jiann-Yang

A2 - Kennedy, Mark William

A2 - Seshadri, Varadarajan

A2 - Zhao, Baojun

A2 - Gregurek, Dean

A2 - Jiang, Tao

A2 - Pistorius, P. Chris

A2 - Keskinkilic, Ender

A2 - Yucel, Onuralp

PB - Springer International Publishing

T2 - 8th International Symposium on High-Temperature Metallurgical Processing, in conjunction with the TMS Annual Meeting and Exhibition, 2017

Y2 - 26 February 2017 through 2 March 2017

ER -

Ertürk S, Sezer R, Hizli İG, Bilen A, Arslan C. Roasting of celestite in laboratory scale rotary furnace. In Hwang JY, Kennedy MW, Seshadri V, Zhao B, Gregurek D, Jiang T, Pistorius PC, Keskinkilic E, Yucel O, editörler, 8th International Symposium on High-Temperature Metallurgical Processing, 2017. Springer International Publishing. 2017. p. 469-476. (Minerals, Metals and Materials Series). doi: 10.1007/978-3-319-51340-9_46

Roasting of celestite in laboratory scale rotary furnace

Özet

Yayın serisi

???event.eventtypes.event.conference???

Bibliyografik not

Finansman

Belgeye Erişim

Diğer Dosyalar ve Linkler

Parmak izi

Alıntı Yap