Recovery of aluminium and its compounds with hydro and pyrometalurgical methods from non-metallic residue

In this study, some experiments were performed for the dimensional control, pre-treatment, getting salt, metallic aluminum and aluminum oxide into the solution of 15, kg aluminum black dross obtained from a private company which recycles aluminium drosses. Water leaching experiments are done for removing salts and aluminum nitride. Temperature stirring speed, solid-liquid rate are investigated while water leaching experiments. Removing of AlN is provided at 25, °C at a rate of 42.48%, at 80, °C at a rate of 86.4%. Leaching experiments performed with NaOH. NaOH concentration and time was analyzed. Efficiency of including metallic aluminum into the solution is determined to be 98% approximately. Melting (fusion) experiments were performed with NaOH at high temperatures to include aluminum oxide in the structure of the remaining after dissolving process into the solution and after dissolving the resulting structures in water, efficiency of including aluminum into the solution is determined to be 85%.