Özet

Some oil-based samples having oxygen, ester, amide, acid and/or hydroxyl structure were prepared for using as lubricants in PVC extrusion. After characterization studies, all samples were tested in PVC formulation using Brabender W50 EHT Lab-Station mixer and extruder. The results were compared with that of a commercial product. From the mixer results, it can be noted that energy consumption was lowered for samples containing acid and amide structures. Surface roughness and opacity of the products were improved when the extruder screw speed was increased from 20 rpm to 60 rpm.

Orijinal dil	İngilizce
Sayfa (başlangıç-bitiş)	237-244
Sayfa sayısı	8
Dergi	Macromolecular Symposia
Hacim	228
DOI'lar	https://doi.org/10.1002/masy.200551021
Yayın durumu	Yayınlandı - Ağu 2005

Belgeye Erişim

10.1002/masy.200551021

Diğer Dosyalar ve Linkler

Link to publication in Scopus

Alıntı Yap

@article{00a29ee1165c4754ae02dfa463d25f50,

title = "Production of viscosity improvers for PVC",

abstract = "Some oil-based samples having oxygen, ester, amide, acid and/or hydroxyl structure were prepared for using as lubricants in PVC extrusion. After characterization studies, all samples were tested in PVC formulation using Brabender W50 EHT Lab-Station mixer and extruder. The results were compared with that of a commercial product. From the mixer results, it can be noted that energy consumption was lowered for samples containing acid and amide structures. Surface roughness and opacity of the products were improved when the extruder screw speed was increased from 20 rpm to 60 rpm.",

keywords = "Additives, Lubricants, Mixer, PVC",

author = "Taner Bostanci and G{\"u}ner, \{F. Seniha\} and Tuncer Erciyes",

year = "2005",

month = aug,

doi = "10.1002/masy.200551021",

language = "English",

volume = "228",

pages = "237--244",

journal = "Macromolecular Symposia",

issn = "1022-1360",

}

TY - JOUR

T1 - Production of viscosity improvers for PVC

AU - Bostanci, Taner

AU - Güner, F. Seniha

AU - Erciyes, Tuncer

PY - 2005/8

Y1 - 2005/8

N2 - Some oil-based samples having oxygen, ester, amide, acid and/or hydroxyl structure were prepared for using as lubricants in PVC extrusion. After characterization studies, all samples were tested in PVC formulation using Brabender W50 EHT Lab-Station mixer and extruder. The results were compared with that of a commercial product. From the mixer results, it can be noted that energy consumption was lowered for samples containing acid and amide structures. Surface roughness and opacity of the products were improved when the extruder screw speed was increased from 20 rpm to 60 rpm.

AB - Some oil-based samples having oxygen, ester, amide, acid and/or hydroxyl structure were prepared for using as lubricants in PVC extrusion. After characterization studies, all samples were tested in PVC formulation using Brabender W50 EHT Lab-Station mixer and extruder. The results were compared with that of a commercial product. From the mixer results, it can be noted that energy consumption was lowered for samples containing acid and amide structures. Surface roughness and opacity of the products were improved when the extruder screw speed was increased from 20 rpm to 60 rpm.

KW - Additives

KW - Lubricants

KW - Mixer

KW - PVC

UR - https://www.scopus.com/pages/publications/25644445257

U2 - 10.1002/masy.200551021

DO - 10.1002/masy.200551021

M3 - Article

AN - SCOPUS:25644445257

SN - 1022-1360

VL - 228

SP - 237

EP - 244

JO - Macromolecular Symposia

JF - Macromolecular Symposia

ER -

Production of viscosity improvers for PVC

Özet

Belgeye Erişim

Diğer Dosyalar ve Linkler

Parmak izi

Alıntı Yap