Production and refining of magnesium metal from turkey originating dolomite

Yeliz Demiray*, Onuralp Yücel

*Bu çalışma için yazışmadan sorumlu yazar

Araştırma sonucu: Dergiye katkıMakalebilirkişi

5 Atıf (Scopus)

Özet

In this study crown magnesium produced from Turkish calcined dolomite by the Pigeon Process was refined and corrosion tests were applied. By using factsage thermodynamic program metalothermic reduction behavior of magnesium oxide and silicate formation structure during this reaction were investigated. After thermodynamic studies were completed, calcination of dolomite and it's metalothermic reduction at temperatures of 1473 K, 1523 K and within a vacuum (varied from 20 to 200 Pa) and refining of crown magnesium was studied. Different flux compositions consisting of MgCl2, KCl, CaCl 2, MgO, CaF 2, NaCl, and SiO 2 with and without B 2O 3 additions were selected for the refining process. These tests were carried out at 963 K for 15, 30 and 45 minutes setting time. Considerable amount of iron was transferred into the sludge phase and its amount decreased from 0.08% to 0.027%. This refined magnesium was suitable for the production of various magnesium alloys. As a result of decreasing iron content, minimum corrosion rate of refined magnesium was obtained 2.35 g=m2=day. The results are compared with previous studies.

Orijinal dilİngilizce
Sayfa (başlangıç-bitiş)251-257
Sayfa sayısı7
DergiHigh Temperature Materials and Processes
Hacim31
Basın numarası3
DOI'lar
Yayın durumuYayınlandı - Haz 2012

Parmak izi

Production and refining of magnesium metal from turkey originating dolomite' araştırma başlıklarına git. Birlikte benzersiz bir parmak izi oluştururlar.

Alıntı Yap