Processing, mechanical and nuclear characterization of boron carbide ceramics consolidated by spark plasma sintering

M. Cengiz, S. C. Ozer, B. Buyuk, A. B. Tugrul, O. Yucel, G. Goller, F. C. Sahin*

*Bu çalışma için yazışmadan sorumlu yazar

Araştırma sonucu: ???type-name???Makalebilirkişi

4 Atıf (Scopus)

Özet

Boron carbide (B4C) ceramics were produced by spark plasma sintering technique with 5, 10, 15, and 20 vol.% aluminum (Al) in order to improve sintering behaviours of B4C ceramics. B4C ceramics were produced, having square cross-section and 50×50×5 mm3 dimensions. The sintering process was carried out at different temperatures by applying 40 MPa of pressure with 100 °C/min under vacuum. The effects of various amounts of Al additive and sintering temperature on density, vickers hardness, fracture toughness and microstructure were examined. The hardness and fracture toughness of the samples were evaluated by the Vickers indentation technique. Microstructures of the samples were characterized by scanning electron microscopy technique. Fast neutron attenuation properties of the ceramics having highest density were also investigated.

Orijinal dilİngilizce
Sayfa (başlangıç-bitiş)187-189
Sayfa sayısı3
DergiActa Physica Polonica A
Hacim128
Basın numarası2
DOI'lar
Yayın durumuYayınlandı - Ağu 2015

Parmak izi

Processing, mechanical and nuclear characterization of boron carbide ceramics consolidated by spark plasma sintering' araştırma başlıklarına git. Birlikte benzersiz bir parmak izi oluştururlar.

Alıntı Yap