Araştırma sonucu: Kitap/Rapor/Konferans Bildirisinde BölümKonferans katkısıbilirkişi

1 Atıf (Scopus)

Özet

The crystal structure of the synthesized magnetic nanoparticles was analyzed with XRD and SEM. Effect of doping value on microstructure was analyzed by XRD. Results are shown in Figure 1. The average particles sizes of samples were obtained by nanosize measure of Zeta Sizer Nano-ZS instrument results at room temperature. Particle size determined within 42-57 nm given Table 1.

Orijinal dilİngilizce
Ana bilgisayar yayını başlığı2013 International Workshop on Magnetic Particle Imaging, IWMPI 2013
DOI'lar
Yayın durumuYayınlandı - 2013
Harici olarak yayınlandıEvet
Etkinlik2013 International Workshop on Magnetic Particle Imaging, IWMPI 2013 - Berkeley, CA, United States
Süre: 23 Mar 201324 Mar 2013

Yayın serisi

Adı2013 International Workshop on Magnetic Particle Imaging, IWMPI 2013

???event.eventtypes.event.conference???

???event.eventtypes.event.conference???2013 International Workshop on Magnetic Particle Imaging, IWMPI 2013
Ülke/BölgeUnited States
ŞehirBerkeley, CA
Periyot23/03/1324/03/13

Parmak izi

Preparation, structure, and magnetic properties of CuMnFe2O 4 nanoparticles for magnetic particle imaging' araştırma başlıklarına git. Birlikte benzersiz bir parmak izi oluştururlar.

Alıntı Yap