Preparation of zinc oxide nanostructures from zinc sulfate and zinc nitrate precursors

Sebahattin Gurmen*, Burcak Ebin, Burak Ozkal

*Bu çalışma için yazışmadan sorumlu yazar

Araştırma sonucu: ???type-name???Konferans katkısıbilirkişi

5 Atıf (Scopus)

Özet

ZnO nanostructures were prepared from zinc sulfate and zinc nitrate precursors by ultrasonic spray pyrolysis (USP) method in air atmosphere condition at 800°C reaction temperature. Effects of the precursor's properties on the morphology, size and chemical features of the products were investigated. Energy dispersive spectroscopy (EDS) was performed to determine the chemical composition of prepared structures. Though, directly producing of the ZnO nanostructures using zinc nitrate precursor by USP method was possible, it was understood that extra heat treatment was necessary to obtain ZnO structures when zinc sulphate precursor was used. The size, shape, and surface morphology of samples were characterized by scanning electron microscope (SEM) revealed that agglomerated 30-50 nm sized nanoparticles were obtained from zinc nitrate precursor. Also, flat like shaped ZnO nanostructures were formed by using zinc sulfate precursor.

Orijinal dilİngilizce
Ana bilgisayar yayını başlığıTMS 2009 - 138th Annual Meeting and Exhibition - Supplemental Proceedings
Sayfalar607-612
Sayfa sayısı6
Yayın durumuYayınlandı - 2009
EtkinlikTMS 2009 - 138th Annual Meeting and Exhibition - San Francisco, CA, United States
Süre: 15 Şub 200919 Şub 2009

Yayın serisi

AdıTMS Annual Meeting
Hacim3

???event.eventtypes.event.conference???

???event.eventtypes.event.conference???TMS 2009 - 138th Annual Meeting and Exhibition
Ülke/BölgeUnited States
ŞehirSan Francisco, CA
Periyot15/02/0919/02/09

Parmak izi

Preparation of zinc oxide nanostructures from zinc sulfate and zinc nitrate precursors' araştırma başlıklarına git. Birlikte benzersiz bir parmak izi oluştururlar.

Alıntı Yap