Physical Properties and Environmental Impact of Sound Barrier Materials Based on Fly Ash Cenosphere

Hui Xie*, Yajing Li, Ercan Kahya, Bo Wang*, Xiyun Ge, Guanda Li

*Bu çalışma için yazışmadan sorumlu yazar

Araştırma sonucu: ???type-name???Makalebilirkişi

4 Atıf (Scopus)

Özet

Traffic noise and solid waste pollution are two major problems that restrict urban development and affect urban environments. In this study, a new kind of cement-based material for sound barriers was prepared using industrial waste fly ash cenosphere to explore the material ratio of the sound absorption, sound insulation, and composite layers and to optimize the material’s properties. The research findings showed that the compressive strength had significant effects on the material properties of the sound absorption layer, with the optimal compressive strength range being 0.2–0.4 MPa. At 0.4 MPa, the material with an aggregate-to-binder ratio of 1.0 had the best comprehensive properties. The sound insulation layer had the best compressive strength of 29.00 MPa at a 45% fiber admixture. The composite had the best sound insulation when the thickness ratio of the sound absorption and insulation layers was 60:40, and the sound transmission loss was 38 dB. The embodied carbon (EC) and embodied energy (EE) of the new fly ash cenosphere across the whole life cycle were 57.57 kgCO2e and 477.08 MJ, respectively, which were 4.8−52.9% and 53.2−82.3% lower than other traditional sound barriers, respectively. Thus, they were environmentally friendly and had satisfactory energy-saving and environmental protection values.

Orijinal dilİngilizce
Makale numarası322
DergiBuildings
Hacim12
Basın numarası3
DOI'lar
Yayın durumuYayınlandı - Mar 2022
Harici olarak yayınlandıEvet

Bibliyografik not

Publisher Copyright:
© 2022 by the authors. Licensee MDPI, Basel, Switzerland.

Finansman

Funding: This research was funded by Science, Technology and Innovation Commission of Shenzhen Municipality grant number [JSGG20191129110221063].

FinansörlerFinansör numarası
Science, Technology and Innovation Commission of Shenzhen MunicipalityJSGG20191129110221063

    Parmak izi

    Physical Properties and Environmental Impact of Sound Barrier Materials Based on Fly Ash Cenosphere' araştırma başlıklarına git. Birlikte benzersiz bir parmak izi oluştururlar.

    Alıntı Yap