Oxygen-loss in A-site deficient Sr0.85La0.10TiO 3 perovskite

Ipek Akin, Ming Li, Zhilun Lu, Derek C. Sinclair*

*Bu çalışma için yazışmadan sorumlu yazar

Araştırma sonucu: Dergiye katkıMakalebilirkişi

26 Atıf (Scopus)

Özet

The electrical properties of Sr1-3xLa2xTiO 3 ceramics (x = 0.05, LST) change dramatically with sintering temperature and atmosphere. Ceramics sintered at 1200 °C in both O 2 and N2 exhibit near intrinsic band-type conduction with bulk conductivity ∼10-7 S cm-1 at 500 °C and activation energy for conduction, Ea of ∼1.6-1.8 eV. LST ceramics sintered at 1450 °C in O2 exhibit much higher bulk conductivity (>10-4 S cm-1 at -50 °C) with an Ea ∼ 0.16 eV. For LST ceramics sintered at 1450 °C in N2, the bulk conductivity was too high to be measured by impedance spectroscopy even at 10 K. In addition, electrical heterogeneity is observed in LST pellets sintered at 1450 °C under both O2 and N2 where pellet outer surfaces are more resistive than the inner regions of the ceramic. The defect chemistry of Sr0.85La0.10TiO3 perovskite is discussed based on chemical doping and oxygen-loss mechanisms and we highlight the importance of A-site vacancies on the oxygen-loss mechanism in La-doped ST-based ceramics.

Orijinal dilİngilizce
Sayfa (başlangıç-bitiş)32549-32554
Sayfa sayısı6
DergiRSC Advances
Hacim4
Basın numarası61
DOI'lar
Yayın durumuYayınlandı - 2014

Parmak izi

Oxygen-loss in A-site deficient Sr0.85La0.10TiO 3 perovskite' araştırma başlıklarına git. Birlikte benzersiz bir parmak izi oluştururlar.

Alıntı Yap