Molten salt synthesis and optical properties of Eu³⁺, Dy³⁺or Nd³⁺ doped NiNb₂O₆ columbite-type phosphors

Abstract Pure, Eu³⁺, Dy³⁺ or Nd³⁺-doped NiNb₂O₆ powders have been prepared by a molten salt synthesis method by using Li₂SO₄-Na₂SO₄ salt mixture as a flux at relatively low temperatures as compared to the solid state reaction method. X-ray diffraction patterns of pure NiNb₂O₆ samples indicated an orthorhombic single phase. For Eu³⁺-doped NiNb₂O₆ samples, the luminescence of Eu³⁺ was observed at 615 nm as red emission while Dy³⁺-doped NiNb₂O₆ showed yellow emission at 577 nm and Nd³⁺ doped sample exhibited a typical emission at 1064 nm varying with the Eu³⁺ or Nd³⁺ doping concentrations. These luminescence characteristics of the doped samples may be attributed to the energy transfer between rare earth ions and NiO₆ octahedral groups in the columbite structure.