Iron-nickel-cobalt (Fe-Ni-Co) alloy particles prepared by ultrasonic spray pyrolysis and hydrogen reduction (USP-HR) method

Cigdem Toparli, Burcak Ebin, Sebahattin Gürmen

Araştırma sonucu: ???type-name???Konferans katkısıbilirkişi

5 Atıf (Scopus)

Özet

Nanocrystalline FeNiCo ternary alloy particles were synthesized by ultrasonic spray pyrolysis and hydrogen reduction method. Fe(NO 3)3.9H2O, Ni(NO3) 2.6H2O and Co(NO3)2.6H2O were used as a starting material to synthesize the nanocrystalline spherical ternary alloy particles. The experiments were performed at 600, 800 and 1000°C using iron-nickel-cobalt nitrate aqueous solution. Shape, morphology, size, chemical composition and crystal structure of the particles were investigated. X-ray diffraction (XRD), scanning electron microscope (FEG-SEM) and energy dispersive spectroscopy (EDS) studies were carried out to characterize the ternary alloys particles. Vibrating sample magnetometer (VSM) was used to characterize the magnetic properties. Spherical nanocrystalline FeNiCo ternary alloy particles were prepared in the size range of 65 and 500 nm. Average crystallite size of the particles is 50 nm.

Orijinal dilİngilizce
Ana bilgisayar yayını başlığıProcessing and Properties of Advanced Ceramics and Composites V
Sayfalar247-254
Sayfa sayısı8
Yayın durumuYayınlandı - 2013
EtkinlikProcessing and Properties of Advanced Ceramics and Composites V - Materials Science and Technology 2012 Conference, MS and T 2012 - Pittsburgh, PA, United States
Süre: 7 Eki 201212 Eki 2012

Yayın serisi

AdıCeramic Transactions
Hacim240
ISSN (Basılı)1042-1122

???event.eventtypes.event.conference???

???event.eventtypes.event.conference???Processing and Properties of Advanced Ceramics and Composites V - Materials Science and Technology 2012 Conference, MS and T 2012
Ülke/BölgeUnited States
ŞehirPittsburgh, PA
Periyot7/10/1212/10/12

Parmak izi

Iron-nickel-cobalt (Fe-Ni-Co) alloy particles prepared by ultrasonic spray pyrolysis and hydrogen reduction (USP-HR) method' araştırma başlıklarına git. Birlikte benzersiz bir parmak izi oluştururlar.

Alıntı Yap