Investigation of the Effects of Spark Plasma Sintering Parameters on Equiatomic CoCrFeNiMo High Entropy Alloy

Aybuke Izci, Baris Yavas, Iulian Antoniac, Gultekin Goller*

*Bu çalışma için yazışmadan sorumlu yazar

Araştırma sonucu: ???type-name???Makalebilirkişi

1 Atıf (Scopus)

Özet

In this study, the effects of sintering temperatures and pressures on densification, crystalline phases, microstructural characterization and mechanical properties of mechanical alloyed equimolar CoCrFeNiMo HEA were investigated. The alloy was composed of major BCC and minor FCC solid solutions coexisting after 40 h of milling. Increasing milling time caused to increase in lattice strain and a decrease in crystallite size. Furthermore, sintering temperature and pressure resulted in the decomposition of the BCC metastable phase and the formation of intermetallic phases and the FCC phase. Herein, increasing sintering temperature and pressure led to decrease lattice strain and increase crystallite size. Moreover, sintering temperature and pressure caused to formation of new intermetallic phases in HEA2 and HEA3. Results revealed that increasing sintering temperatures and pressures of equimolar CoCrFeNiMo end up with a reduction of large pore, enhancement of density value from 7.53 ± 0.02 to 8.78 ± 0.005 g/cm3, hardness from 3.915 to 8.316 GPa, and increment of wear rate from 21.8 × 10−7 to 57.6 × 10−7 mm3/Nm.

Orijinal dilİngilizce
DergiJournal of Materials Engineering and Performance
DOI'lar
Yayın durumuKabul Edilmiş/Basında - 2023

Bibliyografik not

Publisher Copyright:
© 2023, ASM International.

Finansman

This work was supported by Scientific Research Project Funds of Istanbul Technical University (Project Number: FHD-2022-44284). Authors are thankful to H. Huseyin Sezer, Erdem Balci for their assistance with SEM studies, SPS experiments, respectively and Assoc. Prof. Ioana Csaki, who contributes during powder preparation. We wish Assoc. Prof. Ioana Csaki rest in peace.

FinansörlerFinansör numarası
Istanbul Teknik ÜniversitesiFHD-2022-44284

    Parmak izi

    Investigation of the Effects of Spark Plasma Sintering Parameters on Equiatomic CoCrFeNiMo High Entropy Alloy' araştırma başlıklarına git. Birlikte benzersiz bir parmak izi oluştururlar.

    Alıntı Yap