High temperature abrasive wear behavior of an as-cast ductile iron

Ozgur Celik; Hayrettin Ahlatci; E. Sabri Kayali; Huseyin Cimenoglu

doi:10.1016/j.wear.2004.09.004

High temperature abrasive wear behavior of an as-cast ductile iron

Ozgur Celik
, Hayrettin Ahlatci
, E. Sabri Kayali
, Huseyin Cimenoglu^*

^*Bu çalışma için yazışmadan sorumlu yazar

Metalurji ve Malzeme Müh.Böl.

Istanbul Technical University

Araştırma çıktısı: Dergi yayını › Makale › Hakem

42 Atıf (Scopus)

Özet

In this study, high temperature abrasive wear behavior of a GGG 40 quality as-cast ductile iron was examined. Wear tests were performed under a compression stress of 5.7N/mm², by rubbing the samples (pins) on A₂O₃ abrasive grains at various temperatures in between 25 and 600°C. The examined ductile iron exhibited the highest resistance to abrasion at temperature range between 50 and 100°C. Tensile tests carried out at 100°C revealed occurrence of serrated flow on the stress-strain curve, which is the indication of strain aging.

Orijinal dil	İngilizce
Sayfa (başlangıç-bitiş)	189-193
Sayfa sayısı	5
Dergi	Wear
Hacim	258
Basın numarası	1-4 SPEC. ISS.
DOI'lar	https://doi.org/10.1016/j.wear.2004.09.004
Yayın durumu	Yayınlandı - Oca 2005

Belgeye Erişim

10.1016/j.wear.2004.09.004

Diğer Dosyalar ve Linkler

Link to publication in Scopus

Alıntı Yap

@article{6dec4a645f3b4ceab77e42d942828241,

title = "High temperature abrasive wear behavior of an as-cast ductile iron",

abstract = "In this study, high temperature abrasive wear behavior of a GGG 40 quality as-cast ductile iron was examined. Wear tests were performed under a compression stress of 5.7N/mm2, by rubbing the samples (pins) on A2O3 abrasive grains at various temperatures in between 25 and 600°C. The examined ductile iron exhibited the highest resistance to abrasion at temperature range between 50 and 100°C. Tensile tests carried out at 100°C revealed occurrence of serrated flow on the stress-strain curve, which is the indication of strain aging.",

keywords = "Abrasion, Ductile iron, High temperature, Strain aging, Tensile test, Wear",

author = "Ozgur Celik and Hayrettin Ahlatci and Kayali, \{E. Sabri\} and Huseyin Cimenoglu",

year = "2005",

month = jan,

doi = "10.1016/j.wear.2004.09.004",

language = "English",

volume = "258",

pages = "189--193",

journal = "Wear",

issn = "0043-1648",

publisher = "Elsevier B.V.",

number = "1-4 SPEC. ISS.",

}

TY - JOUR

T1 - High temperature abrasive wear behavior of an as-cast ductile iron

AU - Celik, Ozgur

AU - Ahlatci, Hayrettin

AU - Kayali, E. Sabri

AU - Cimenoglu, Huseyin

PY - 2005/1

Y1 - 2005/1

N2 - In this study, high temperature abrasive wear behavior of a GGG 40 quality as-cast ductile iron was examined. Wear tests were performed under a compression stress of 5.7N/mm2, by rubbing the samples (pins) on A2O3 abrasive grains at various temperatures in between 25 and 600°C. The examined ductile iron exhibited the highest resistance to abrasion at temperature range between 50 and 100°C. Tensile tests carried out at 100°C revealed occurrence of serrated flow on the stress-strain curve, which is the indication of strain aging.

AB - In this study, high temperature abrasive wear behavior of a GGG 40 quality as-cast ductile iron was examined. Wear tests were performed under a compression stress of 5.7N/mm2, by rubbing the samples (pins) on A2O3 abrasive grains at various temperatures in between 25 and 600°C. The examined ductile iron exhibited the highest resistance to abrasion at temperature range between 50 and 100°C. Tensile tests carried out at 100°C revealed occurrence of serrated flow on the stress-strain curve, which is the indication of strain aging.

KW - Abrasion

KW - Ductile iron

KW - High temperature

KW - Strain aging

KW - Tensile test

KW - Wear

UR - https://www.scopus.com/pages/publications/10444258043

U2 - 10.1016/j.wear.2004.09.004

DO - 10.1016/j.wear.2004.09.004

M3 - Article

AN - SCOPUS:10444258043

SN - 0043-1648

VL - 258

SP - 189

EP - 193

JO - Wear

JF - Wear

IS - 1-4 SPEC. ISS.

ER -

High temperature abrasive wear behavior of an as-cast ductile iron

Özet

Belgeye Erişim

Diğer Dosyalar ve Linkler

Parmak izi

Alıntı Yap