Hard and tough α-SiAION ceramics

M. J. Hoffmann, Hasan Mandal

Araştırma sonucu: Dergiye katkıMakalebilirkişi

14 Atıf (Scopus)

Özet

Yb, Nd/Ca and Ce/Ca containing a-sialon starting compositions have been densified by either pressureless sintering or capsul free sinter/HIP'ing using "conventional" α-Si3N4 powder. X-ray diffraction studies of both compositions after sintering revealed that only a-sialon was observed as a matrix phase. Microstructural characterization of the relatively high nitrogen rich starting composition resulted in a typical equiaxed grain morphology, as expected. But the relatively less nitrogen rich starting composition exhibited surprisingly an elongated grain morphology with typical grain length of 5-20 urn and aspect ratios of 4-15. The mechanical property measurements on the material with equiaxed grains showed a hardness value of 19.76 GPa and a toughness value of 3.96 MPam"2 as expected. The a-sialon material with elongated grains proved to have a hardness value of 19.30 GPa (HV10) but fracture toughness value of 6.31 MPam . Crack deflection, crack bridging and grain pull-out mechanisms were accounted for the significant improvement in fracture toughness. ©2000 Trans Tech Publications,.
Orijinal dilİngilizce
Sayfa (başlangıç-bitiş)219-224
Sayfa sayısı6
DergiMaterials Science Forum
Hacim325-326
DOI'lar
Yayın durumuYayınlandı - 2000

Parmak izi

Hard and tough α-SiAION ceramics' araştırma başlıklarına git. Birlikte benzersiz bir parmak izi oluştururlar.

Alıntı Yap