Galvaniz tesislerinde olusan sivi atiklarin metalurjik olarak degerlendirilmesi

Mehmet Şeref Sönmez*, Ercan Açma

*Bu çalışma için yazışmadan sorumlu yazar

Araştırma sonucu: ???type-name???Makalebilirkişi

2 Atıf (Scopus)

Özet

In this study, the treatment of waste pickling liquor which was taken from a hot dip galvanizing process was investigated. The steps of the process used for the treatment of this solution were goethite precipitation, zinc carbonate precipitation, the production of useful products from precipitates and discharge of the final solution. In the experiments, the optimum parameters of these process steps were investigated. All of the iron was oxidized to Fe3+ by the addition of H2O2. Following oxidation, NaOH neutralization was performed to increase pH of solution to 2.5, which resulted in complete precipitation of the iron as goethite. The total required time for the complete precipitation of the iron was 20-25 minutes. Yellow-colored β-goethite was converted to α-Fe2O3 by dehydration at a temperature of 250°C. In the solution from which iron had been eliminated, zinc was precipitated completely by the addition of Na2CO3. The precipitated product was ZnCO3 and relatively pure ZnO was produced by the calcination of this product for 0.5 hr at 300°C.

Tercüme edilen katkı başlığıMetallurgical evaluation of liquor wastes of galvanizing plants
Orijinal dilTürkçe
Sayfa (başlangıç-bitiş)53-68
Sayfa sayısı16
DergiTurkish Journal of Engineering and Environmental Sciences
Hacim24
Basın numarası1
Yayın durumuYayınlandı - 2000

Keywords

  • Goethite precipitation
  • Hot galvanizing
  • Waste pickling liquors