Failure of a 17-4 PH stainless steel sailboat propeller shaft

C. Fahir Arisoy; Gokhan Başman; M. Kelami Şeşen

doi:10.1016/S1350-6307(03)00041-4

Failure of a 17-4 PH stainless steel sailboat propeller shaft

C. Fahir Arisoy
, Gokhan Başman
, M. Kelami Şeşen^*

^*Bu çalışma için yazışmadan sorumlu yazar

Metalurji ve Malzeme Müh.Böl.

Istanbul Technical University

Araştırma sonucu: Dergiye katkı › Makale › bilirkişi

80 Atıf (Scopus)

Özet

In this study, a 17-4 PH precipitation hardening stainless steel propeller shaft failed in use when installed in a sailboat working in a marine environment. Failure analysis was conducted on the propeller shaft. Results indicate that the failure was caused by the fracture of the propeller shaft by torsional fatigue and stress corrosion cracking (SCC). SCC progressed transgranulary in the martensitic matrix.

Orijinal dil	İngilizce
Sayfa (başlangıç-bitiş)	711-717
Sayfa sayısı	7
Dergi	Engineering Failure Analysis
Hacim	10
Basın numarası	6
DOI'lar	https://doi.org/10.1016/S1350-6307(03)00041-4
Yayın durumu	Yayınlandı - Ara 2003

Belgeye Erişim

10.1016/S1350-6307(03)00041-4

Diğer Dosyalar ve Linkler

Link to publication in Scopus

Alıntı Yap

@article{35c46d908aa740958b988e9e2db3a216,

title = "Failure of a 17-4 PH stainless steel sailboat propeller shaft",

abstract = "In this study, a 17-4 PH precipitation hardening stainless steel propeller shaft failed in use when installed in a sailboat working in a marine environment. Failure analysis was conducted on the propeller shaft. Results indicate that the failure was caused by the fracture of the propeller shaft by torsional fatigue and stress corrosion cracking (SCC). SCC progressed transgranulary in the martensitic matrix.",

keywords = "Failure analysis, Fatigue, Martensite, Shafts, Stress corrosion cracking",

author = "Arisoy, \{C. Fahir\} and Gokhan Ba{\c s}man and {\c S}e{\c s}en, \{M. Kelami\}",

year = "2003",

month = dec,

doi = "10.1016/S1350-6307(03)00041-4",

language = "English",

volume = "10",

pages = "711--717",

journal = "Engineering Failure Analysis",

issn = "1350-6307",

publisher = "Elsevier B.V.",

number = "6",

}

TY - JOUR

T1 - Failure of a 17-4 PH stainless steel sailboat propeller shaft

AU - Arisoy, C. Fahir

AU - Başman, Gokhan

AU - Şeşen, M. Kelami

PY - 2003/12

Y1 - 2003/12

N2 - In this study, a 17-4 PH precipitation hardening stainless steel propeller shaft failed in use when installed in a sailboat working in a marine environment. Failure analysis was conducted on the propeller shaft. Results indicate that the failure was caused by the fracture of the propeller shaft by torsional fatigue and stress corrosion cracking (SCC). SCC progressed transgranulary in the martensitic matrix.

AB - In this study, a 17-4 PH precipitation hardening stainless steel propeller shaft failed in use when installed in a sailboat working in a marine environment. Failure analysis was conducted on the propeller shaft. Results indicate that the failure was caused by the fracture of the propeller shaft by torsional fatigue and stress corrosion cracking (SCC). SCC progressed transgranulary in the martensitic matrix.

KW - Failure analysis

KW - Fatigue

KW - Martensite

KW - Shafts

KW - Stress corrosion cracking

UR - https://www.scopus.com/pages/publications/0142259697

U2 - 10.1016/S1350-6307(03)00041-4

DO - 10.1016/S1350-6307(03)00041-4

M3 - Article

AN - SCOPUS:0142259697

SN - 1350-6307

VL - 10

SP - 711

EP - 717

JO - Engineering Failure Analysis

JF - Engineering Failure Analysis

IS - 6

ER -

Failure of a 17-4 PH stainless steel sailboat propeller shaft

Özet

Belgeye Erişim

Diğer Dosyalar ve Linkler

Parmak izi

Alıntı Yap