Failure Analysis of Fencing Blades

D. Kibaroglu, M. Baydogan, H. Cimenoglu, B. Bas, C. Yagsi, N. Aliyeva

Araştırma sonucu: ???type-name???Konferans makalesibilirkişi

1 Atıf (Scopus)

Özet

This study deals with the failure analysis of broken fencing blades (one épée and one foil). For the characterization of the broken blades, metallographic examinations, chemical analysis, hardness measurements, fracture surface examinations and tensile tests were performed. Maximum stress occurred at the outer fibres of the blades was estimated as high as 1456 MPa and 1298 MPa for épée and foil, respectively. Results showed that failure of the blades was initiated from a notch, which has been formed as the result of an impact action during training, or from the groove machined along the blade for inserting an electrical wire. In order to increase resistance of the blades against such failures, alternative blade material, modified blade geometry and a surface hardening treatment were proposed.

Orijinal dilİngilizce
Makale numarası012009
DergiJournal of Physics: Conference Series
Hacim843
Basın numarası1
DOI'lar
Yayın durumuYayınlandı - 31 May 2017
Etkinlik6th International Conference on Fracture Fatigue and Wear, FFW 2017 - Porto, Portugal
Süre: 26 Tem 201727 Tem 2017

Bibliyografik not

Publisher Copyright:
© Published under licence by IOP Publishing Ltd.

Parmak izi

Failure Analysis of Fencing Blades' araştırma başlıklarına git. Birlikte benzersiz bir parmak izi oluştururlar.

Alıntı Yap