Failure Analysis of ATV Axles

Başar Yavuz; Murat Vural

doi:10.1007/s11668-022-01366-0

Failure Analysis of ATV Axles

Başar Yavuz^*
, Murat Vural

^*Bu çalışma için yazışmadan sorumlu yazar

Makina Mühendisliği Bölümü

Piri Reis University

Araştırma sonucu: Dergiye katkı › Makale › bilirkişi

Özet

In this study, failure analysis of the axle of a 4-wheeled vehicle was carried out. The part broke during daily use, causing an accident. The axle is made of 4340 alloy steel material. In order to understand the cause of the damage, visual inspection, and then, fatigue analysis was performed. As a result of visual inspection, signs of fatigue damage were observed. The analysis was advanced based on this initial information. As a result, it was concluded that the damage was due to the sudden load caused by fatigue.

Orijinal dil	İngilizce
Sayfa (başlangıç-bitiş)	676-679
Sayfa sayısı	4
Dergi	Journal of Failure Analysis and Prevention
Hacim	22
Basın numarası	2
DOI'lar	https://doi.org/10.1007/s11668-022-01366-0
Yayın durumu	Yayınlandı - Nis 2022

Bibliyografik not

Publisher Copyright:
© 2022, ASM International.

Belgeye Erişim

10.1007/s11668-022-01366-0

Diğer Dosyalar ve Linkler

Link to publication in Scopus

Alıntı Yap

@article{bb009935f9d842de8d3bd37cac15ccba,

title = "Failure Analysis of ATV Axles",

abstract = "In this study, failure analysis of the axle of a 4-wheeled vehicle was carried out. The part broke during daily use, causing an accident. The axle is made of 4340 alloy steel material. In order to understand the cause of the damage, visual inspection, and then, fatigue analysis was performed. As a result of visual inspection, signs of fatigue damage were observed. The analysis was advanced based on this initial information. As a result, it was concluded that the damage was due to the sudden load caused by fatigue.",

keywords = "Axle failure, Failure analysis, Fatigue, Residual stress",

author = "Ba{\c s}ar Yavuz and Murat Vural",

note = "Publisher Copyright: {\textcopyright} 2022, ASM International.",

year = "2022",

month = apr,

doi = "10.1007/s11668-022-01366-0",

language = "English",

volume = "22",

pages = "676--679",

journal = "Journal of Failure Analysis and Prevention",

issn = "1547-7029",

publisher = "Springer New York",

number = "2",

}

TY - JOUR

T1 - Failure Analysis of ATV Axles

AU - Yavuz, Başar

AU - Vural, Murat

PY - 2022/4

Y1 - 2022/4

N2 - In this study, failure analysis of the axle of a 4-wheeled vehicle was carried out. The part broke during daily use, causing an accident. The axle is made of 4340 alloy steel material. In order to understand the cause of the damage, visual inspection, and then, fatigue analysis was performed. As a result of visual inspection, signs of fatigue damage were observed. The analysis was advanced based on this initial information. As a result, it was concluded that the damage was due to the sudden load caused by fatigue.

AB - In this study, failure analysis of the axle of a 4-wheeled vehicle was carried out. The part broke during daily use, causing an accident. The axle is made of 4340 alloy steel material. In order to understand the cause of the damage, visual inspection, and then, fatigue analysis was performed. As a result of visual inspection, signs of fatigue damage were observed. The analysis was advanced based on this initial information. As a result, it was concluded that the damage was due to the sudden load caused by fatigue.

KW - Axle failure

KW - Failure analysis

KW - Fatigue

KW - Residual stress

UR - https://www.scopus.com/pages/publications/85125817273

U2 - 10.1007/s11668-022-01366-0

DO - 10.1007/s11668-022-01366-0

M3 - Article

AN - SCOPUS:85125817273

SN - 1547-7029

VL - 22

SP - 676

EP - 679

JO - Journal of Failure Analysis and Prevention

JF - Journal of Failure Analysis and Prevention

IS - 2

ER -

Failure Analysis of ATV Axles

Özet

Bibliyografik not

Belgeye Erişim

Diğer Dosyalar ve Linkler

Parmak izi

Alıntı Yap