Fabrication and characterization of polysulfone reinforced hollow fibre membrane

Turker Turken, Reyhan Sengur-Tasdemir, Gulsum Melike Urper-Bayram, Oguz Gunes, Esra Ates-Genceli, Volodymyr V. Tarabara, Ismail Koyuncu*

*Bu çalışma için yazışmadan sorumlu yazar

Araştırma sonucu: ???type-name???Makalebilirkişi

7 Atıf (Scopus)

Özet

In this study, reinforced hollow fibre membranes were fabricated using different molecular weights of polyvinylidene prolidone (PVP Mw: 10, 40 and 360 kDa) and different take-up speeds (1, 2, 2.6 and 3.5 m/min). Prepared reinforced hollow fibre membranes were characterized in terms of permeability; surface morphology and hydrophilicity; pore size distribution; bovine serum albumin (BSA) rejection and flux recovery ratio. Optimum permeability and BSA rejection were obtained when PVP molecular weight was 40 kDa. After PVP molecular weight determination, advancing speed was changed and it was seen that increasing advancing speed ended up with decreased membrane wall thickness; however, decreased wall thickness increased the probability of irreversible fouling.

Orijinal dilİngilizce
Sayfa (başlangıç-bitiş)2690-2699
Sayfa sayısı10
DergiEnvironmental Technology (United Kingdom)
Hacim42
Basın numarası17
DOI'lar
Yayın durumuYayınlandı - 2021

Bibliyografik not

Publisher Copyright:
© 2020 Informa UK Limited, trading as Taylor & Francis Group.

Finansman

The authors are grateful to TUBITAK (Türkiye Bilimsel ve Teknolojik Araştirma Kurumu) (The Scientific and Technological Research Council of Turkey) for their financial support under grant number 113Y359. The collaboration between ITU and MSU teams was supported in part by the U. S. National Science Foundation Partnerships for International Research and Education programme [grant number 1243433].

FinansörlerFinansör numarası
U. S. National Science Foundation Partnerships for International Research and Education programme1243433
International Technological University
Türkiye Bilimsel ve Teknolojik Araştirma Kurumu113Y359
Midlands State University

    Parmak izi

    Fabrication and characterization of polysulfone reinforced hollow fibre membrane' araştırma başlıklarına git. Birlikte benzersiz bir parmak izi oluştururlar.

    Alıntı Yap