Fabrication and characterization of Ni-W solid solution alloys via mechanical alloying and pressureless sintering

Keyphrases

• Microhardness 100%
• Mechanical Alloying 100%
• Pressureless Sintering 100%
• Ni-W 100%
• Solid Solution Alloy 100%
• W Content 100%
• X-ray Diffraction Pattern 66%
• Sintered Sample 66%
• Flow Condition 33%
• H2 Gas 33%
• Scanning Electron Microscope 33%
• Wear Experiment 33%
• Ar Gas 33%
• Microstructural Characterization 33%
• Mechanically Alloying 33%
• Crystallite Size 33%
• Relative Density 33%
• Gas Flow 33%
• Alloy Powder 33%
• Density Value 33%
• Electron Backscatter Diffraction 33%
• Intermetallic Phases 33%
• Sintered Compacts 33%
• Compression Test 33%
• High Relative Density 33%
• Ni-W Alloy 33%
• Powder Compact 33%
• Sliding Wear 33%
• Ni Powder 33%
• Solid Solution Phase 33%
• Room Temperature Compression 33%

Material Science

• Mechanical Alloying 100%
• Microhardness 100%
• Sintering 100%
• Solid Solutions 100%
• X-Ray Diffraction 66%
• Density 66%
• Diffraction Pattern 66%
• Scanning Electron Microscopy 33%
• Sliding Wear 33%
• Alloying 33%
• Crystallite Size 33%
• Intermetallic Compound 33%
• Electron Backscatter Diffraction 33%
• Sintering of Powder 33%
• Phase Composition 33%