Enhanced photocatalytic activity of highly transparent superhydrophilic doped TiO₂ thin films for improving the self-cleaning property of solar panel covers

Undoped and metal doped nanocrystalline TiO₂ transparent thin films were synthesized on glass substrates via sol-gel/dip-coating method. TiO₂ thin film coatings can be applied to the surfaces of solar panels to impart self-cleaning properties to them. The structural and optical properties of few nanometer-thick films were characterized by XRD, SEM, CA, AFM, XPS, and UV–Vis spectrophotometry techniques. The stoichiometric TiO₂ films crystallized in anatase phase, with a particle size of ∼100 nm, which were uniformly distributed on the surface. The prepared films with a roughness of ∼1–5 nm, increased the hydrophilicity of the glass surface. Reducing the amount of Ti precursor (X) favored the improvement of film quality. To improve the photocatalytic activity of the TiO₂ thin film, it was doped with Ni, Cd, Mo, Bi and Sr metal ions. The effect of metal doping on the photocatalytic activity of the films was investigated using the degradation process of methylene blue (MB) dye as the model contaminant. Among the prepared coatings, the Sr–TiO₂ film showed the highest efficiency for MB degradation. It increased the dye degradation efficiency of the films under both UV and Vis lights. The kinetic investigations also showed that the degradation of MB by TiO₂ and M − TiO₂ films obeyed the pseudo-first order kinetics.