Electrodeposition of zinc and reduced graphene oxide on porous nickel electrodes for high performance supercapacitors

İbrahim Yılmaz, Ali Gelir, Onder Yargi*, Utkan Sahinturk, Oguz Kaan Ozdemir

*Bu çalışma için yazışmadan sorumlu yazar

Araştırma sonucu: Dergiye katkıMakalebilirkişi

11 Atıf (Scopus)

Özet

Electrochemical properties of porous nickel (Ni) foam, electrodeposited zinc (Zn) on Ni foam (Ni–Zn) and electrodeposited reduced graphene oxide (rGO) on Ni–Zn foam electrodes (Ni–Zn-rGO) in 6 M KOH electrolyte were investigated. Cyclic voltammetry (CV) and galvanostatic charge–discharge cycling (GCD) techniques were used to carry out the redox interactions, and cycling capacitive properties of the electrodes in KOH solution. Platinum (Pt) and gold (Au) foil were used as a counter electrode and the current collector in the electrochemical measurements, respectively. The specific capacitances of the electrodes were found from the GCD measurements as 155, 722 and 1820 F/g for Ni, Ni–Zn and Ni–Zn/rGO electrodes at the current density of 1 A/g, respectively. Scanning electron microscope (SEM) images of the three electrodes were also taken into account to associate all the electrochemical measurements. These results clearly show that specific capacitance values highly increased after the deposition of Zn and rGO to Ni electrode.

Orijinal dilİngilizce
Makale numarası109307
DergiJournal of Physics and Chemistry of Solids
Hacim138
DOI'lar
Yayın durumuYayınlandı - Mar 2020

Bibliyografik not

Publisher Copyright:
© 2019

Parmak izi

Electrodeposition of zinc and reduced graphene oxide on porous nickel electrodes for high performance supercapacitors' araştırma başlıklarına git. Birlikte benzersiz bir parmak izi oluştururlar.

Alıntı Yap