Electrical and dielectric properties of foam injection-molded polypropylene/multiwalled carbon nanotube composites

A combination of high dielectric permittivity (ε′) and low dielectric lob (tan δ) is required for charge storage applications. In percolative systems such as conductive polymer composites, however, obtaining high ε′ and low tan δ is very challenging due to the sharp insulation-conduction transition near the threshold region. Due to the particular arrangement of conductive fillers induced by both foaming and injection molding procebes, they may addreb this ibue. Therefore, this work evaluates the application of foam injection molding proceb in fabricating polymer nanocomposites for energy storage. Polypropylene-multiwalled carbon nanotubes (PP-MWCNT) composites were prepared by melt mixing and foamed in an injection molding proceb. Electrical conductivity (σ), ε′ and tan δ were then characterized. Also, scanning and transmibion electron microscopy (SEM and TEM) was used to investigate the carbon nanotube's arrangement as well as cellular morphology. The results showed that foam injection-molded composites exhibited highly superior dielectric properties to those of solid counterparts. For instance, foamed samples had ε′=68.3 and tan δ =0.05 (at 1.25 vol.% MWCNT), as opposed to ε′=17.8 and tan δ=0.04 in solid samples (at 2.56 vol.% MWCNT). The results of this work reveal that high performance dielectric nanocomposites can be developed using foam injection molding technologies for charge storage applications.