Effect of temperature and film thickness on microstructure and residual stress for YbBCO-coated conductors

L. Arda*, S. Ataoglu

*Bu çalışma için yazışmadan sorumlu yazar

Araştırma sonucu: ???type-name???Makalebilirkişi

10 Atıf (Scopus)

Özet

The rare-earth mixed oxide (Gd1-xHox)2O3 and the superconductor YbBa2Cu3O7-x were prepared by sol-gel synthesis using metal-organic precursors. Textured Gd1.802Ho0.198O3 buffer layers were grown on biaxially textured Ni (1 0 0) substrates. YbBa2Cu3O7-x layers were epitaxially grown on the Gd1.802Ho0.198O3-coated Ni substrates using the reel-to-reel sol-gel dip coating system. Different thicknesses of superconducting layers, annealed at various temperatures, were tried to observe the effects of thickness and temperature on residual stress and microstructure properties. Residual stress in the YbBCO/Gd1.802Ho0.198O3/Ni was calculated analytically. The results showed that variation of residual stress along the thickness of structure (Ni substrate, buffer layer and YbBCO film) was constant. We also observed that the Ni substrate is under tension while buffer layer was under compression in the case of without YbBCO layer. However the residual stress was under compression in the case of YbBCO in all layers. The surface morphologies and microstructure of all samples were characterized by environmental scanning electron microscope (ESEM), atomic force microscope (AFM) and X-ray diffraction (XRD). The pole figure texture analyses of Ni substrate, Gd1.802Ho0.198O3 buffer layers and YbBCO film have shown a single cube-on-cube textured structure.

Orijinal dilİngilizce
Sayfa (başlangıç-bitiş)282-290
Sayfa sayısı9
DergiJournal of Alloys and Compounds
Hacim471
Basın numarası1-2
DOI'lar
Yayın durumuYayınlandı - 5 Mar 2009

Parmak izi

Effect of temperature and film thickness on microstructure and residual stress for YbBCO-coated conductors' araştırma başlıklarına git. Birlikte benzersiz bir parmak izi oluştururlar.

Alıntı Yap