Effect of sintering temperature on mechanical and microstructural properties of bovine hydroxyapatite (BHA)

G. Goller, F. N. Oktar*, S. Agathopoulos, D. U. Tulyaganov, J. M.F. Ferreira, E. S. Kayali, I. Peker

*Bu çalışma için yazışmadan sorumlu yazar

Araştırma sonucu: ???type-name???Makalebilirkişi

92 Atıf (Scopus)

Özet

The influence of sintering temperature on densification, microstructure and the mechanical properties of bovine hydroxyapatite (BHA), produced by a calcination method, was investigated. Densification and mechanical properties improved with increasing sintering temperature in the range between 1000°C and 1300°C, with optimum properties being obtained at a sintering temperature of 1200°C. The measured mechanical properties indicate that sintered BHA bodies are interesting biomaterials for further investigation in biomedical applications.

Orijinal dilİngilizce
Sayfa (başlangıç-bitiş)111-115
Sayfa sayısı5
DergiJournal of Sol-Gel Science and Technology
Hacim37
Basın numarası2
DOI'lar
Yayın durumuYayınlandı - Şub 2006

Parmak izi

Effect of sintering temperature on mechanical and microstructural properties of bovine hydroxyapatite (BHA)' araştırma başlıklarına git. Birlikte benzersiz bir parmak izi oluştururlar.

Alıntı Yap