Effect of annealing temperature on structural and magnetic properties of Zn0.94Co0.05Cu0.01O

Z. K. Heiba, L. Arda, Mohamed Bakr Mohamed*, Nasser Y. Mostafa, N. Dogan

*Bu çalışma için yazışmadan sorumlu yazar

Araştırma sonucu: ???type-name???Makalebilirkişi

28 Atıf (Scopus)

Özet

The doped ZnO system Zn0.94Co0.05Cu0.01O (ZCCO) was prepared as a nano-polycrystalline by a simple sol-gel process, then air annealed at different temperatures. Applying X-ray diffraction (XRD) and the Rietveld method, structural analysis showed that Co and Cu replace Zn substitutionally yielding ZCCO single phase. The refined u-fractional coordinate of Zn increases monotonically by an annealing temperature from 0.3546 at 500°C reaching 0.3722 at 800°C, very near from the ideal value 0.375. The Zn tetrahedrons become more symmetric and the distortion is gradually relieved by annealing up to 800°C. Annealing at 900°C introduces tetrahedron distortion in an opposite way. The zero field cooled (ZFC) and field cooled (FC) magnetization versus the temperature at different applied fields and the magnetization versus the applied field at different temperatures were carried out. The system exhibits a ferromagnetic behavior at room temperature. As the annealing temperature increases from 550 to 900°C, the saturation magnetization at 300 K increases from 0.0507 to 0.1088 emu/g.

Orijinal dilİngilizce
Sayfa (başlangıç-bitiş)3487-3493
Sayfa sayısı7
DergiJournal of Superconductivity and Novel Magnetism
Hacim26
Basın numarası12
DOI'lar
Yayın durumuYayınlandı - Ara 2013
Harici olarak yayınlandıEvet

Parmak izi

Effect of annealing temperature on structural and magnetic properties of Zn0.94Co0.05Cu0.01O' araştırma başlıklarına git. Birlikte benzersiz bir parmak izi oluştururlar.

Alıntı Yap