title = "Effect of aging and thermomechanical processes in twin roll cast MG AZ91 alloy sheet",
abstract = "6 mm thick and 1500 mm wide magnesium alloy AZ91 sheet was produced by twin roll casting. Sheets were homogenized between 350-475°C for 1-24 h. Afterwards, they were warm rolled down to 2.75 mm. Age hardening was also performed on twin roll cast AZ91 alloy sheets. Specimens were aged at 150, 200 and 250°C for up to 100 h. Characterization was performed by light microscope, TEM-EDS, and XRD after twin roll casting and also after each fhermomechanical process including aging. Tensile tests were performed for mechanical properties. Moreover, the age-hardening response of Mg AZ91 alloy was examined by micro hardness test.",
keywords = "Aging, AZ91, Fhermomechanical processes, Magnesium alloy, Twin roll casting",
author = "Ozgur Duygulu and Selda Ucuncuoglu and Gizem Oktay and Onuralp Yucel and Kaya, \{Ali Arslan\}",
year = "2010",
language = "English",
isbn = "9780873397469",
series = "Magnesium Technology",
pages = "527--532",
booktitle = "Magnesium Technology 2010 - Held During TMS 2010 Annual Meeting and Exhibition",
note = "Magnesium Technology 2010 - TMS 2010 Annual Meeting and Exhibition ; Conference date: 14-02-2010 Through 18-02-2010",
}