Crystalline phase effect on the up-conversion processes and white emission of Yb3+/Er3+/Tm3+:Y2Si2O7 nanocrystals

Murat Erdem*, Sevcan Tabanli, Gonul Eryurek, Ramazan Samur, Baldassare DI Bartolo

*Bu çalışma için yazışmadan sorumlu yazar

Araştırma sonucu: ???type-name???Makalebilirkişi

15 Atıf (Scopus)

Özet

Yb3+,Er3+,Tm3+:Y2Si2O7 nanopowders were fabricated by a sol-gel method and then annealed at two different temperatures of 1050 °C and 1480 °C for 12 h to investigate the phase effect on the structural and optical properties. X-ray diffraction patterns (XRD) of all powders revealed that most of the peaks were in good harmony with the standard JCPDS cards of Y2Si2O7 (PDF #38-0223 and PDF #38-0440). SEM images of the powders were taken to examine the morphology and chemical composition of the powders. Diffuse reflection spectra of Y2Si2O7 exhibited varying number of transitions depending on the dopant ion in all powders in the range of 400-1050 nm. The spectral properties of the powders were investigated to identify the possible up-conversion (UC) emission mechanism in the range between 400 and 900 nm under 975 nm excitation. A broadening white light emission was observed with increasing laser pumping power at room temperature as well. Spectral profiles of the transitions observed in both reflectance and up-conversion luminescence spectra were found to be crystalline phase dependent.

Orijinal dilİngilizce
Sayfa (başlangıç-bitiş)6464-6472
Sayfa sayısı9
DergiDalton Transactions
Hacim48
Basın numarası19
DOI'lar
Yayın durumuYayınlandı - 2019

Bibliyografik not

Publisher Copyright:
© 2019 The Royal Society of Chemistry.

Finansman

This study was financially supported by the Scientific Research Projects Unit (BAPKO) of Marmara University with the project number FEN-A-080715-0339.

FinansörlerFinansör numarası
Marmara ÜniversitesiFEN-A-080715-0339
Firat University Scientific Research Projects Management Unit

    Parmak izi

    Crystalline phase effect on the up-conversion processes and white emission of Yb3+/Er3+/Tm3+:Y2Si2O7 nanocrystals' araştırma başlıklarına git. Birlikte benzersiz bir parmak izi oluştururlar.

    Alıntı Yap