Corrosion resistance of as-plated and heat-treated electroless dublex Ni-P/Ni-B-W coatings

Behiye Yüksel*, Garip Erdogan, Fatih Erdem Bastan, Rasid Ahmed Yýldýz

*Bu çalışma için yazışmadan sorumlu yazar

Araştırma sonucu: ???type-name???Makalebilirkişi

2 Atıf (Scopus)

Özet

In this study, Ni-P/Ni-B-W dublex coatings were deposited on carbon steel substrates (AISI 1020) using the electroless plating process and their microstructure and corrosion properties were systematically evaluated based on different heat-treatment temperatures. Both, the surface morphology and cross-sectional morphology of the Ni-P/Ni-B-W coatings were studied using a scanning electron microscope (SEM), while X-ray diffraction (XRD) was applied for examining the structural modifications. The amorphous coating began to crystallize at a heat-treatment temperature of 350 °C. Potentiodynamic polarization measurements were carried out in an aqueous medium containing 3.5 % NaCl for evaluating the corrosion resistance of as-plated and heat-treated dublex coatings. The corrosion potentials of dublex coatings were observed to shift toward more positive values with increased heat-treatment temperatures. Depending on the heat-treatment temperature, it was identified that the crystallized dublex coatings generally had better corrosion resistance than the amorphous coating.

Orijinal dilİngilizce
Sayfa (başlangıç-bitiş)837-842
Sayfa sayısı6
DergiMateriali in Tehnologije
Hacim51
Basın numarası5
DOI'lar
Yayın durumuYayınlandı - 2017

Parmak izi

Corrosion resistance of as-plated and heat-treated electroless dublex Ni-P/Ni-B-W coatings' araştırma başlıklarına git. Birlikte benzersiz bir parmak izi oluştururlar.

Alıntı Yap