Copolymers and terpolymers of vinyl phosphonic acid, acrylonitrile, methyl acrylate, and vinyl acetate. Thermal oxidative stabilization and their nanofiber

Elif Keskin, Nesrin Köken*, Nilgün Kızılcan, Ahmet Akar

*Bu çalışma için yazışmadan sorumlu yazar

Araştırma sonucu: ???type-name???Makalebilirkişi

Özet

Copolymers and terpolymers of acrylonitrile (AN), methyl acrylate (MA), vinyl acetate (VA), and vinyl phosphonic acid (VPA) were synthesized. Thermal gravimetric analysis studies showed that the decomposition of PANMAVPA and PANVAVPA terpolymers started at lower temperatures than PANMA and PANVA copolymers. VPA and MA caused an increase in the ring formation of pendant nitrile groups and the total ash content of PANMAVPA terpolymer. During the thermal oxidative treatment (TOS) of PANVAVPA, the phosphonic acid moiety accelerated double bond formation via acetic acid elimination. 151–340 nm nanofibers were successfully produced from copolymers and terpolymers.

Orijinal dilİngilizce
Sayfa (başlangıç-bitiş)2030-2042
Sayfa sayısı13
DergiPolymer-Plastics Technology and Materials
Hacim62
Basın numarası15
DOI'lar
Yayın durumuYayınlandı - 2023

Bibliyografik not

Publisher Copyright:
© 2023 Taylor & Francis.

Finansman

The work was supported by the the Scientific and Technical Research Council of Turkey (TUBITAK) 2244 Industrial Ph.D. Program -Istanbul Technical University-Arcelik Project No: 118C104. [ITU BAP; Project No.: TDK-2021-43296]. The authors would like to thank the Scientific and Technical Research Council of Turkey (TUBITAK) 2244 Industrial Ph.D. Program -Istanbul Technical University-Arçelik Project No: 118C104. The authors acknowledge funding from the Research Fund of the Istanbul Technical University, Turkey (ITU BAP; Project No.: TDK-2021-43296). The authors would like to thank the Scientific and Technical Research Council of Turkey (TUBITAK) 2244 Industrial Ph.D. Program -Istanbul Technical University-Arçelik Project No: 118C104. The authors acknowledge funding from the Research Fund of the Istanbul Technical University, Turkey (ITU BAP; Project No.: TDK-2021-43296).

FinansörlerFinansör numarası
Istanbul Technical University, Turkey
Istanbul Technical University-Arcelik
Istanbul Technical University-Arçelik118C104
Türkiye Bilimsel ve Teknolojik Araştırma Kurumu
Bilimsel Araştırma Projeleri Birimi, İstanbul Teknik ÜniversitesiTDK-2021-43296

    Parmak izi

    Copolymers and terpolymers of vinyl phosphonic acid, acrylonitrile, methyl acrylate, and vinyl acetate. Thermal oxidative stabilization and their nanofiber' araştırma başlıklarına git. Birlikte benzersiz bir parmak izi oluştururlar.

    Alıntı Yap