Au/TiO 2 nanorod-based Schottky-type UV photodetectors

Hakan Karaagac*, Levent Erdal Aygun, Mehmet Parlak, Mohammad Ghaffari, Necmi Biyikli, Ali Kemal Okyay

*Bu çalışma için yazışmadan sorumlu yazar

Araştırma sonucu: ???type-name???Makalebilirkişi

26 Atıf (Scopus)

Özet

TiO 2 nanorods (NRs) were synthesized on fluorine-doped tin oxide (FTO) pre-coated glass substrates using hydrothermal growth technique. Scanning electron microscopy studies have revealed the formation of vertically-aligned TiO 2 NRs with length of ~2 μm and diameter of 110-128 nm, homogenously distributed over the substrate surface. 130 nm thick Au contacts using thermal evaporation were deposited on the n-type TiO 2 NRs at room temperature for the fabrication of NR-based Schottky-type UV photodetectors. The fabricated Schottky devices functioned as highly sensitive UV photodetectors with a peak responsivity of 134.8 A/W (λ = 350 nm) measured under 3 V reverse bias.

Orijinal dilİngilizce
Sayfa (başlangıç-bitiş)442-444
Sayfa sayısı3
DergiPhysica Status Solidi - Rapid Research Letters
Hacim6
Basın numarası11
DOI'lar
Yayın durumuYayınlandı - Kas 2012
Harici olarak yayınlandıEvet

Parmak izi

Au/TiO 2 nanorod-based Schottky-type UV photodetectors' araştırma başlıklarına git. Birlikte benzersiz bir parmak izi oluştururlar.

Alıntı Yap