Annealing ambient effect on electrical properties of ZnO:Al/p-Si heterojunctions

Osman Urper, Ozge Karacasu, Huseyin Cimenoglu, Nilgun Baydogan*

*Bu çalışma için yazışmadan sorumlu yazar

Araştırma sonucu: ???type-name???Makalebilirkişi

14 Atıf (Scopus)

Özet

Aluminum doped zinc oxide (ZnO:Al) thin films via 1.2 at. % Al content was deposited on p-type silicon wafers by using sol-gel dip coating technique to compare the effect of post treatment ambient on electrical characteristics of ZnO:Al/p-Si heterojunction. The annealing environment treatment was performed at 700 °C for 60 min under various gas ambients such as, air, argon, nitrogen, and vacuum. The deposited heterojunction samples were characterised in order to clarified its morphology and crystalline structure. The films showed an orientation along c-axis and the best electrical properties (0.75 × 10−4 Ω cm) were obtained for the sample prepared in vacum. The changes in electrical properties and current-voltage performance were compared with each other after p-n junction was annealed under different ambient conditions. The heterojunction electrical parameters were determined Therefore, it was possible to make an annealing ambient comparison of the heterojunction for the cost-effect production by using sol-gel dip coating technique to use as the diode in electronic devices.

Orijinal dilİngilizce
Sayfa (başlangıç-bitiş)81-87
Sayfa sayısı7
DergiSuperlattices and Microstructures
Hacim125
DOI'lar
Yayın durumuYayınlandı - Oca 2019

Bibliyografik not

Publisher Copyright:
© 2018 Elsevier Ltd

Parmak izi

Annealing ambient effect on electrical properties of ZnO:Al/p-Si heterojunctions' araştırma başlıklarına git. Birlikte benzersiz bir parmak izi oluştururlar.

Alıntı Yap