Özet
The aim of this investigation was to develop lustre glazed Iznik tiles and characterization of nanoclusters which is responsible for the metallic shine in the lustre layer. Traditional Iznik tiles having high quartz content body and lead-alkali glaze were produced using laboratory controlled conditions. Lustre paste was applied on the surfaces of these tiles by brush. These lustre paste applied Iznik tiles were then fired under oxidizing and reducing atmosphere. The characterization of lustre layers were carried out using numerous different analytical techniques such as SEM, WDXRF, XRD, XPS, UV–vis–NIR, AFM and TEM–EDS.
| Orijinal dil | İngilizce |
|---|---|
| Sayfa (başlangıç-bitiş) | 11489-11497 |
| Sayfa sayısı | 9 |
| Dergi | Ceramics International |
| Hacim | 41 |
| Basın numarası | 9 |
| DOI'lar | |
| Yayın durumu | Yayınlandı - Kas 2015 |
Bibliyografik not
Publisher Copyright:© 2015 Elsevier Ltd and Techna Group S.r.l.
Finansman
This research was funded by the TUBITAK 1001 (The Support Program for Scientific and Technological Research Projects) project entitled as “Advancing Iznik Tiles (Our Cultural Heritage) to 21 st century by Applying Nano-Science and Advanced Nano-Structured Materials-110M190”. The authors are grateful to TUBITAK for financial support and Prof. Sevim Çizer for valuable discussions. Thanks are also due to Prof. Dr. Mehmet Ali Gülgün and Dr. Meltem Sezen of the Sabancı University Nanotechnology Research and Application Center (SUNUM) for their valuable support in Analytical-TEM investigations. We are also grateful to Dr. Melek Türksoy of the Gebze Institute of Technology Nanotechnology Research Center for XPS analysis. Many thanks to Cem Berk from TUBITAK MRC Materials Institute for SEM examinations and Emre Karabeyoğlu for XRD and XRF analysis.
| Finansörler | Finansör numarası |
|---|---|
| TUBITAK | |
| TUBITAK 1001 |